Dielectric ceramic composition for low temperature sintering and multilayer ceramic capacitor using the same
The invention relates to a dielectric ceramic composition, which can be sintered at a low temperature as well as achieve a high dielectric constant with excellent thermal stability, and a multilayer ceramic capacitor using the same. The dielectric ceramic composition comprises a main component of (Ba 1−x Ca x ) m TiO 3 ; and sub-components including MgCO 3 , RE 2 O 3 , MO, MnO, V 2 O 5 , Cr 2 O 3 and a sintering additive of SiO 2 . RE 2 O 3 is at least one selected from the rare earth oxide group consisting of Y 2 O 3 , Dy 2 O 3 and Ho 2 O 3 , and MO is one of Ba and Ca. The dielectric ceramic composition is expressed by a following formula: a(Ba 1−x Ca x ) m TiO 3 -bMgCO 3 -cRE 2 O 3 -dMO-eMnO-fSiO 2 -gV 2 O 5 -hCr 2 O 3 . Here, a, b, c, d, e, f, g, and h satisfy following relationships: in mole fraction, a=100, 0.1≦b≦3.0, 0.1≦c≦3.0, 0.1≦d≦3.0, 0.05≦e≦1.0, 0.2≦f≦3.0, 0.01≦g≦1.0, and 0.01≦h≦1.0, and x and m satisfy following relationships: 0.005≦x≦0.15, and 0.995≦m≦1.03.
1. A dielectric ceramic composition comprising:
a main component of (Ba 1−x Ca x ) m TiO 3 ; and
sub-components of MgCO 3 , RE 2 O 3 , MO, MnO, V 2 O 5 , Cr 2 O 3 and a sintering additive of SiO 2 , where RE 2 O 3 is at least one selected from the rare earth oxide group consisting of Y 2 O 3 , Dy 2 O 3 and Ho 2 O 3 , and MO is one of Ba and Ca,
wherein the dielectric ceramic composition is expressed by a following formula: a(Ba 1−x Ca x ) m TiO 3 -bMgCO 3 -cRE 2 O 3 -dMO-eMnO-fSiO 2 -gV 2 O 5 -hCr 2 O 3 , where a, b, c, d, e, f, g, and h satisfy following relationships: in mole fraction, a=100, 0.1≦b≦3.0, 0.1≦c≦3.0, 0.1≦d≦3.0, 0.05≦e≦1.0, 0.2≦f≦3.0, 0.01≦g≦1.0, and 0.01≦h≦1.0, and x and m satisfy following relationships: 0.005≦x≦0.15, and 0.995≦m≦1.03.
2. The dielectric ceramic composition according to claim 1 , wherein the (Ba 1−x Ca x ) m TiO 3 component is provided by (Ba 1−x Ca x ) m TiO 3 powder having a mean particle size ranging from 150 nm to 400 nm.
3. The dielectric ceramic composition according to claim 1 , wherein the (Ba 1−x Ca x ) m TiO 3 component is provided by (Ba 1−x Ca x ) m TiO 3 powder produced by at least one selected from the group consisting of solid state mixing, hydrothermal synthesis and sol-gel method.
4. The dielectric ceramic composition according to claim 1 , wherein m added with d is larger than 1.00 and smaller than 1.03.
5. The dielectric ceramic composition according to claim 1 , wherein the SiO 2 component is provided by SiO 2 powder.
6. The dielectric ceramic composition according to claim 1 , wherein the SiO 2 component is provided by SiO 2 sol or Si alkoxide.
7. A multilayer ceramic capacitor comprising a capacitor body having dielectric layers and internal electrodes alternating with the dielectric layers,
wherein each of the dielectric layers comprises a main component of (Ba 1−x Ca x ) m TiO 3 , and sub-components of MgCO 3 , RE 2 O 3 , MO, MnO, V 2 O 5 , Cr 2 O 3 and a sintering additive of SiO 2 , where RE 2 O 3 is at least one rare earth oxide selected from the group consisting of Y 2 O 3 , Dy 2 O 3 and Ho 2 O 3 , MO is one of Ba and Ca, and
wherein the composition of the dielectric layers is expressed by a following formula: a(Ba 1−x Ca x ) m TiO 3 -bMgCO 3 -cRE 2 O 3 -dMO-eMnO-fSiO 2 -gV 2 O 5 -hCr 2 O 3 , where a, b, c, d, e, f, g, and h satisfy following relationships: in mole fraction, a=100, 0.1≦b ≦3.0, 0.1≦c≦3.0, 0.1≦d≦3.0, 0.05≦e≦1.0, 0.2≦f≦3.0, 0.01≦g≦1.0, and 0.01≦h≦1.0, and x and m satisfy following relationships: 0.005≦x≦0.15, and 0.995≦m≦1.03.
8. The multilayer ceramic capacitor according to claim 7 , wherein the internal electrodes contain a conductor of Ni or Ni alloy.
9. The multilayer ceramic capacitor according to claim 7 , wherein the dielectric layers include at least 400 layers stacked one atop another.
10. The multilayer ceramic capacitor according to claim 7 , wherein each of the dielectric layers has a thickness of 3 μm or less.
11. The multilayer ceramic capacitor according to claim 7 , wherein each of the dielectric layers has a thickness of 0.5 μm to 3 μm.
12. The multilayer ceramic capacitor according to claim 7 , wherein the (Ba 1−x Ca x ) m TiO 3 component of the dielectric layers has a mean particle size ranging from 150 nm to 400 nm.