Steel alloy, holders and holder details for plastic moulding tools, and tough hardened blanks for holders and holder details
A steel alloy suitable for holders and holder details for plastic molding tools contains in weight-%: 0.06-0.15 C, 0.07-0.22 N, wherein the total amount of C+N shall satisfy the condition, 0.16≦C+N≦0.26, 0.1-1.0 Si, 0.1-2.0 Mn, 12.5-14.5 Cr, 0.8-2.5 Ni, 0.1 1.5 Mo, optionally vanadium up to max. 0.7 V, optionally, in order to improve the machinability of the steel, one or more of the elements S, Ca and O in amounts up to max. 0.25 S, max. 0.01 (100 ppm) Ca, max. 0.01 (100 ppm) O, balance iron and unavoidable impurities.
1. A steel alloy, consisting essentially of, in weight-%:
0.06-0.14 C,
0.08-0.12 N,
0.18≦C+N≦0.26,
0.1-1.0 Si,
0.1-2.0 Mn,
13.1-13.7 Cr,
1.5-1.7 Ni,
0.4-0.6 Mo,
max. 0.7 V,
0.035-0.15 S, and
balance iron and unavoidable impurities,
wherein, after hardening and tempering, the steel alloy has a substantially martensitic matrix,
wherein, after hardening and tempering, the steel alloy is essentially void of ferrite, and
wherein, after hardening and tempering, the steel alloy is essentially void of spots having a hardness substantially higher than a hardness of the martensitic matrix.
2. The steel alloy according to claim 1 , wherein the steel alloy consists essentially of, in weight-%, 0.07-0.13 C.
3. The steel alloy according to claim 1 , wherein the total amount of C+N satisfies the condition, in weight-%, 0.18<C+N<0.23.
4. The steel alloy according to claim 1 , wherein the steel alloy consists essentially of, in weight-%, 0.1-0.7 Si.
5. The steel alloy according to claim 4 , wherein the steel alloy contains consists essentially of, in weight-%, 0.1-0.4 Si.
6. The steel alloy according to claim 4 , wherein the steel alloy contains consists essentially of, in weight-%, max. 0.5 Si.
7. The steel alloy according to claim 1 , wherein the steel alloy consists essentially of, in weight-%, max. 1.5 Mn.
8. The steel alloy according to claim 7 , wherein the steel alloy consists essentially of, in weight-%, max. 1.3 Mn.
9. The steel alloy according to claim 1 , wherein the steel alloy contains consists essentially of, in weight-%, at least 0.07 V.
10. The steel alloy according to claim 9 , wherein the steel alloy consists essentially of at least 0.10 V.
11. The steel alloy according to claim 10 , wherein the steel alloy consists essentially of, in weight-%, 0.10-0.30 V.
12. The steel alloy according to claim 11 , wherein the steel alloy consists essentially of, in weight-%, 0.10-0.20 V.
13. The steel alloy according to claim 1 , wherein the steel consists essentially of, in weight-%, 0.08-0.12 S.
14. The steel alloy according to claim 1 , wherein the steel alloy consists essentially of, in weight-%:
0.06-0.13 C,
0.1-0.4 Si,
0.2-1.3 Mn, and
0.1-0.3 V.
15. The steel alloy according to claim 14 , wherein the steel alloy consists essentially of, in weight-%, 0.2-0.3 Si.
16. The steel alloy of claim 1 ,
wherein the steel alloy has a hardness, after hardening and tempering, between 280-360 HB.
17. The steel alloy according to claim 16 , wherein the total amount of C+N satisfies the condition, in weight-%, 0.18<C+N<0.25.
18. The steel alloy according to claim 16 , wherein the steel alloy consists essentially of, in weight-%, 0.85-1.8 Mn.
19. The steel alloy according to claim 18 , wherein the steel alloy consists essentially of, in weight-%, 0.97-0.98 Mn.
20. The steel alloy according to claim 18 , wherein the steel alloy consists essentially of, in weight-%, 1.4-1.6 Mn.
21. The steel alloy according to claim 16 , wherein the steel alloy consists essentially of, in weight-%, 13.5-13.7 Cr.
22. The steel alloy according to claim 16 , wherein the steel alloy consists essentially of, in weight-%, at least 0.11 S.
23. The steel alloy according to claim 16 , further consisting essentially of, in weight-%, at least one of max. 0.01 Ca and max. 0.01 O.
24. The steel alloy according to claim 1 , wherein the steel alloy consists essentially of, in weight-%, 0.10-0.14 C.
25. The steel alloy according to claim 24 , wherein the steel alloy consists essentially of, in weight-%, 0.11-0.14 C.
26. The steel alloy according to claim 1 , wherein the steel alloy consists essentially of, in weight-%, 0.75-0.95 Si.
27. The steel alloy according to claim 1 , further consisting essentially of, in weight-%, at least one of max. 0.01 Ca and max. 0.01 O.
28. Holders and holder details for plastic moulding tools comprising the steel alloy according to claim 1 .
29. Holders and holder details for plastic moulding tools comprising the steel alloy according to claim 16 .