Conductive mono atomic layer coatings for fuel cell bipolar plates
View Patent ↗An electrically conductive separator element and assembly for a fuel cell which comprises an electrically conductive substrate having a monoatomic layer coating overlying the substrate. The monatomic layer coating may comprise an electrically conductive material, for example, a noble metal, desirably Ru, Rh, Pd, Ag, Ir, Os and preferably Au. Methods of making such separator elements and assemblies are also provided.
1. An electrically conductive separator element for use in a stack of electrochemical cells, comprising a conductive metal substrate and an ultra-thin coating on said substrate, wherein said coating comprises an electrically conductive material and has an average thickness equal to about the diameter of one atom of the electrically conductive material.
2. A separator element according to claim 1 , wherein the thickness of the coating is from about 0.3 nm to about 0.5 nm.
3. A separator element according to claim 1 , wherein the electrically conductive material comprises a material selected from the group consisting of Au, Ag, Ir, Ru, Rh, Os, Pd, Pt, RuO 2 , IrO 2 and combinations thereof.
4. A separator element according to claim 1 , wherein the electrically conductive material comprises Au.
5. A separator element according to claim 1 , wherein the metal substrate comprises a member selected from the group consisting of stainless steel, aluminum, titanium and foamed conductive metals.
6. A separator element according to claim 1 , wherein said coating has a contact resistance at 50 psi to 200 psi suitable for use in a fuel cell.
7. A separator element according to claim 4 , wherein the coating comprises Au and wherein the contact resistance is from about 7 to about 8 milliohms/cm 2 at pressures from 50 psi to 200 psi.
8. A fuel cell comprising the separator element of claim 1 .
9. An electrically conductive separator assembly for use in a stack of electrochemical cells, comprising:
a first electrically conductive separator element having a first surface and a second electrically conductive separator element having a second surface;
an ultra-thin coating overlying one or more areas of said respective first and said second surfaces, wherein said coating comprises an electrically conductive material and has an average thickness equal to about the diameter of one atom of the electrically conductive material; and
electrically conductive paths formed by physical contact between said coated regions of said first surface and said second surface.
10. The separator assembly according to claim 9 , further comprising lands interspersed with grooves along said respective surfaces, the lands having the overlying ultra-thin coating,
wherein the lands of the first surface are in physical contact with the lands of the second surface, thereby forming electrically conductive paths.
11. A method for manufacturing an electrically conductive separator element for a fuel cell, comprising:
providing an electrically conductive metal substrate, said metal substrate susceptible to formation of metal oxides in the presence of oxygen;
removing any of said metal oxides from a surface of said substrate; and
depositing an ultra-thin coating onto the surface of said substrate, wherein said coating comprises an electrically conductive material and has an average thickness equal to about the diameter of one atom of the electrically conductive material.
12. The method according to claim 11 , wherein said removing and said depositing are conducted essentially simultaneously.
13. The method according to claim 11 , wherein said depositing is conducted by a process selected from the group consisting of electron beam evaporation, physical vapor deposition and atomic layer deposition.
14. The method according to claim 11 , wherein said removing is conducted by a process selected from the group consisting of electrolytic cleaning, etching, pickling, mechanical abrasion, and ion beam sputtering.
15. The method according to claim 11 , wherein said electrically conductive material comprises Au.
16. The method according to claim 13 , wherein said depositing is conducted by electron beam evaporation.
17. The method according to claim 13 , wherein said depositing is conducted by atomic layer deposition.
18. The method according to claim 17 , wherein said atomic layer deposition comprises:
subjecting said substrate to at least one precursor vapor of the electrically conductive material at a temperature sufficiently high for the vapor to react with the surface of said substrate but too high for the vapors to condense on the surface.
19. The method according to claim 17 , wherein the atomic layer deposition is conducted at a temperature between about 150° C. and about 600° C.
20. The method according to claim 17 , wherein the atomic layer deposition is conducted at a pressure between about 7.5×10 −2 Torr and about 4 Torr.