View Patent ↗This invention is directed to an improvement in nonwoven products comprised of a nonwoven web of fibers bonded together with polymeric binder comprised of emulsion polymerized units of vinyl acetate, ethylene, and a crosslinking monomer. The polymer is stabilized with a surfactant having a critical micelle concentration of about 0.5 to 3% by weight. The surfactant is employed in the polymerization in an amount less than 1% by weight, based upon the total weight of polymer.
1. In a nonwoven product comprised of a nonwoven web of fibers bonded together with a sufficient amount of polymeric binder to form a self-sustaining web, said polymeric binder comprised of a polymer containing vinyl acetate, ethylene, and a crosslinking monomer, said polymeric binder formed by emulsion polymerization, the improvement which comprises:
employing a surfactant having a critical micelle concentration of from 0.5 to 3% by weight of said surfactant in said emulsion polymerization and wherein the surfactant is employed in the emulsion polymerization in an amount of less than 1% by weight of the polymeric binder;
said polymer having an ethylene content of from about 3 to 30% by weight, based on the total weight of polymer;
said polymer having a crosslinkable monomer content in an amount of from 1 to 10% by weight, based on the total weight of polymer; and wherein,
said polymer contains from 0.5 to 5% of a copolymerizable, stabilizing monomer based upon the total weight of said polymer.
2. The nonwoven product of claim 1 wherein the copolymerizable stabilizing monomer is selected from the group consisting of sodium vinyl sulfonate and 2-acrylamido-2-methylpropane sulfonic acid.
3. The nonwoven product of claim 1 wherein the critical micelle concentration of said surfactant is from about 1 to 2 percent by weight.
4. The nonwoven product of claim 1 wherein the surfactant employed in the emulsion polymerization is selected from the group consisting of the dihexyl ester sodium sulfosuccinate, sodium 2-ethylhexyl sulfate, sodium isobutyl sulfosuccinate, sodium diamyl sulfosuccinate, sodium dicyclohexyl sulfosuccinate, and sodium diisopropylnaphthalene sulfosuccinate.
5. The nonwoven product of claim 1 wherein the Tg of said polymer is from 5 to 20° C.
6. The nonwoven product of claim 1 wherein said polymer contains from 0.5 to 10% by weight vinyl chloride, based on the total weight of the polymer.
7. The nonwoven product of claim 1 wherein said polymer contains from 3 to 8% by weight vinyl chloride, based on the total weight of the polymer.
8. The nonwoven product of claim 1 wherein said polymer contains from 0.5 to 10% by weight of vinyl versatate, based on the total weight of polymer.
9. The nonwoven product of claim 1 wherein the surfactant employed in the emulsion polymerization is the dihexyl ester of sodium sulfosuccinate.