Method for manufacturing an ignition plug and ignition plug produced in that manner

1. A method for manufacturing a high-energy, low-voltage ignition plug comprising a ceramic material between its electrodes, comprising the steps of:

forming an admixture by mixing in a container containing a liquid, from 50 to 75% by mass of a compound which forms a conductive phase and from 25 to 50% by mass of one or more materials which allow the formation of insulating phases of yttrium garnet after thermal processing;

pulverising, drying and sieving the admixture;

pressing or injecting the admixture into a mould;

carrying out sintering of the admixture so as to obtain a ceramic material having porosity of between 0 and 30%, the sintering of the admixture being carried out under a controlled argon atmosphere; and

using the ceramic material in order to constitute a material located between the electrodes of a high-energy, low-voltage ignition plug.

2. The method according to claim 1 , wherein the materials are selected from SiC and MoSi2 and admixtures thereof.

3. The method according to claim 1 , wherein the porosity of the ceramic material obtained is between 0 and 15% during the sintering of the admixture.

4. The method according to claim 1 , wherein there is added to the admixture a thermoemissive doping agent at a proportion of up to 30% of the total mass of the compounds which are intended to form the conductive phase and the insulating phases.

5. The method according to claim 1 , wherein from 3 to 60% by mass, relative to the total mass of the compounds which are intended to form the conductive phase and the insulating phases, of one or more organic binding or plasticising compounds is added to the admixture, and in that a de-binding operation is carried out after the pressing or injection and before the sintering operation.

6. The method according to claim 5 , wherein the pulverising is carried out in two steps, in that the addition of the plasticising agent is carried out between the two steps and in that the second pulverising step is less energetic than the first step.

7. The method according to claim 1 , wherein the materials which allow the formation of phases of yttrium garnet are aluminium oxide and Y203.

8. The method according to claim 7 , wherein the yttrium garnet is an yttrium aluminium garnet which contains one or more of the compounds Y203, A1203, YAl03, Y3Al5012, Y4Al209.

9. The method according to claim 4 , wherein the thermoemissive doping agent is LaB6.

10. A method for manufacturing a high-energy, low-voltage ignition plug comprising a ceramic material between its electrodes, comprising the steps of:

there is mixed, in a container containing a liquid, from 50 to 75% by mass of a compound which forms a conductive phase and from 25 to 50% by mass of one or more materials which allow the formation of insulating phases of yttrium garnet after thermal processing;

operations are carried out for pulverising, drying and sieving the admixture;

the admixture is pressed or injected into a mould;

sintering of the admixture is carried out so as to obtain a ceramic material having porosity of between 0 and 30%; and

the ceramic material is used in order to constitute the material located between the electrodes of a high-energy, low-voltage ignition plug,

wherein from 3 to 60% by mass, relative to the total mass of the compounds which are intended to form the conductive phase and the insulating phases, of one or more organic binding or plasticising compounds is added to the admixture, and in that a de-binding operation is carried out after the pressing or injection and before the sintering operation.

11. The method according to claim 10 , wherein the pulverising is carried out in two steps, in that the addition of the plasticising agent is carried out between the two steps and in that the second pulverising step is less energetic than the first step.