Functional graphene-polymer nanocomposites for gas barrier applications
A gas diffusion barrier contains a polymer matrix and a functional graphene which displays no signature of graphite and/or graphite oxide, as determined by X-ray diffraction.
1. A gas diffusion barrier, comprising:
a polymer matrix; and
a functional graphene having a surface area of from about 300 m 2 /g to 2600 m 2 /g, wherein said functional graphene is made by thermally exfoliating graphite oxide at a temperature of from 300 to 2000° C.
2. The gas diffusion barrier as claimed in claim 1 , wherein said functional graphene has a bulk density of from about 40 kg/m3 to 0.1 kg/m3.
3. The gas diffusion barrier as claimed in claim 1 , wherein said functional graphene has a C/O oxygen ratio of from about 60/40 to 95/5.
4. The gas diffusion barrier as claimed in claim 1 , comprising 0.1 to 90% by weight of said functional graphene, based on the total weight of said composition.
5. The gas diffusion barrier as claimed in claim 1 , wherein said functional graphene is produced by a process, comprising:
(a) intercalating and oxidizing graphite to obtain graphite oxide; and
(b) heating the graphite oxide to obtain said functional graphene at a temperature of from 300 to 2000° C.
6. The gas diffusion barrier as claimed in claim 1 , wherein said polymer matrix comprises an elastomer.
7. The gas diffusion barrier as claimed in claim 1 , wherein said polymer matrix comprises at least one member selected from the group consisting of polyethylenes, polypropylenes, copolymers ethylene and propylene, polyesters, nylons, polystyrenes, polyvinyl acetates, polycarbonates, polyvinyl chlorides, polymethylmethacrylates, polymethylacrylates, polycaprolactones, polycaprolactams, fluorinated ethylenes, polystyrenes, styrene acrylonitriles, polyimides, epoxys, polyurethanes and mixtures thereof.
8. The gas diffusion barrier as claimed in claim 1 , wherein said polymer matrix comprises an elastomer selected from the group consisting of vulcanized natural rubber, styrene-butadiene rubber, polystyrene-polyisoprene-polystyrene, a polysiloxane and mixtures thereof.
9. The gas diffusion barrier as claimed in claim 1 , which is electrically conductive.
10. The gas diffusion barrier as claimed in claim 1 , wherein said functional graphene is the form of nano platelets.
11. The gas diffusion barrier as claimed in claim 10 , wherein said functional graphene has an aspect ratio of more than 100.
12. A process for manufacturing a gas diffusion barrier, comprising:
adding a functional graphene having a surface area of from about 300 m 2 /g to 2600 m 2 /g, to a polymer matrix,
wherein said functional graphene is made by thermally exfoliating graphite oxide at a temperature of from 300 to 2000° C.
13. The process according to claim 12 , further comprising orienting said functional graphene in said polymer matrix.
14. The process as claimed in claim 12 , wherein said functional graphene has a bulk density of from about 40 kg/m3 to 0.1 kg/m3.
15. The process as claimed in claim 12 , wherein said functional graphene has a C/O oxygen ratio of from about 60/40 to 95/5.
16. The process as claimed in claim 12 , comprising adding 0.1 to 90% by weight of said functional graphene.
17. The gas diffusion barrier as claimed in claim 1 , wherein said functional graphene has a surface area of from about 400 m 2 /g to 2600 m 2 /g.
18. The gas diffusion barrier as claimed in claim 1 , wherein said functional graphene has a surface area of from about 500 m 2 /g to 2600 m 2 /g.
19. The process as claimed in claim 12 , wherein said functional graphene has a surface area of from about 400 m 2 /g to 2600 m 2 /g.
20. The process as claimed in claim 12 , wherein said functional graphene has a surface area of from about 500 m 2 /g to 2600 m 2 /g.