Hollow resin fine particles, organic/inorganic hybrid fine particles, and method for producing hollow resin fine particles
It is the object of the present invention to provide a hollow resin particle and an organic-inorganic hybrid particle, which have excellent dispersibility in a binder component and prevent the diffuse reflection of light and can attain an antireflection layer having high alkali resistance when used as a particle constituting an antireflection layer having a low refractive index, and a method of producing the hollow resin particle.
1. A method of producing a hollow resin particle,
having a single hollow structure and an average particle diameter being 10 to 100 nm,
which comprises:
a step of preparing a dispersion obtained by dispersing a polymerizable droplet containing a species selected from the group consisting of a polyisocyanate, an epoxy prepolymer and an acid halide as lipophilic reaction component A and an organic solvent in a polar medium containing at least one species selected from the group consisting of water, amine, polyol, and polycarboxylic acid as hydrophilic reaction component B;
a step of reacting the lipophilic reaction component A with the hydrophilic reaction component B; and
a step of removing the organic solvent from the resin particle.
2. A method of producing a hollow resin particle,
having a single hollow structure, an average particle diameter being 10 to 100 nm and a composite shell comprising at least two resin layers of an outermost layer and an inner layer,
which comprises:
a step of preparing a dispersion obtained by dispersing a polymerizable droplet containing a species selected from the group consisting of a polyisocyanate, an epoxy prepolymer and an acid halide as lipophilic reaction component A, a lipophilic reaction component C and an organic solvent in a polar medium containing at least one species selected from the group consisting of water, amine, polyol, and polycarboxylic acid as hydrophilic reaction component B;
a step of reacting the lipophilic reaction component A on a surface of the polymerizable droplet with the hydrophilic reaction component B and an organic solvent in the polar medium to form an outermost layer on the surface of the polymerizable droplet;
a step of reacting the lipophilic reaction component C within the polymerizable droplet to form an inner layer; and
a step of removing the organic solvent from the resin particle.
3. A hollow resin particle,
which has a single hollow structure, an average particle diameter being 10-100 nm, a refractive index being 1.40 or less, and a hollow rate being 30% or more,
wherein the hollow resin particle is produced by a method which comprises the steps of:
preparing a dispersion obtained by dispersing a polymerizable droplet containing a lipophilic reaction component A in a polar medium containing a hydrophilic reaction component B; and
reacting the lipophilic reaction component A with the hydrophilic reaction component B.
4. The hollow resin particle according to claim 3 , which has an outermost layer comprising at least a resin obtained by a reaction of a lipophilic reaction component A and a hydrophilic reaction component B.
5. A hollow resin particle,
which has a single hollow structure and a composite shell comprising at least two resin layers of an outermost layer and an inner layer, a hollow rate being 30% or more, an average particle diameter being 10 to 100 nm and a refractive index being 1.40 or less,
wherein the hollow resin particle is produced by a method which comprises the steps of:
preparing a dispersion obtained by dispersing a polymerizable droplet containing a lipophilic reaction component A in a polar medium containing a hydrophilic reaction component B; and
reacting the lipophilic reaction component A with the hydrophilic reaction component B.
6. The hollow resin particle according to claim 5 ,
wherein the outermost layer is composed of a resin obtained by a reaction of a lipophilic reaction component A and a hydrophilic reaction component B, and the inner layer is composed of a resin obtained by a reaction of a lipophilic reaction component C not reacting with the lipophilic reaction component A and the hydrophilic reaction component B.
7. The hollow resin particle according to claim 3 , which contains a fluorine-containing monomer.
8. The hollow resin particle according to claim 3 , wherein the outermost layer contains at least one species of resin selected from the group consisting of polyurea, polyurethane, polyamide, polyester, nylon and epoxy polymer.
9. The hollow resin particle according to claim 3 , which contains a resin crosslinked by an inorganic component.
10. A composition comprising the hollow resin particle according to claim 3 .
11. A composition comprising the hollow resin particle according to claim 5 .
12. A hollow resin particle,
which has a single hollow structure, an average particle diameter being 10-100 nm, a refractive index being 1.40 or less, and a hollow rate being 30% or more,
wherein the hollow resin particle is produced by a method which comprises the steps of:
preparing a dispersion obtained by dispersing a polymerizable droplet containing a lipophilic reaction component A and a lipophilic reaction component C in a polar medium containing a hydrophilic reaction component B;
reacting the lipophilic reaction component A on a surface of the polymerizable droplet with the hydrophilic reaction component B in the polar medium to form an outermost layer on the surface of the polymerizable droplet; and
reacting the lipophilic reaction component C within the polymerizable droplet to form an inner layer.
13. The hollow resin particle according to claim 12 , which has an outermost layer comprising at least a resin obtained by a reaction of a lipophilic reaction component A and a hydrophilic reaction component B.
14. A hollow resin particle,
which has a single hollow structure and a composite shell comprising at least two resin layers of an outermost layer and an inner layer, a hollow rate being 30% or more, an average particle diameter being 10 to 100 nm and a refractive index being 1.40 or less,
wherein the hollow resin particle is produced by a method which comprises the steps of:
preparing a dispersion obtained by dispersing a polymerizable droplet containing a lipophilic reaction component A and a lipophilic reaction component C in a polar medium containing a hydrophilic reaction component B;
reacting the lipophilic reaction component A on a surface of the polymerizable droplet with the hydrophilic reaction component B in the polar medium to form an outermost layer on the surface of the polymerizable droplet; and
reacting the lipophilic reaction component C within the polymerizable droplet to form an inner layer.
15. The hollow resin particle according to claim 14 ,
wherein the outermost layer is composed of a resin obtained by a reaction of a lipophilic reaction component A and a hydrophilic reaction component B, and the inner layer is composed of a resin obtained by a reaction of a lipophilic reaction component C not reacting with the lipophilic reaction component A and the hydrophilic reaction component B.
16. The hollow resin particle according to claim 12 , which contains a fluorine-containing monomer.
17. The hollow resin particle according to claim 12 , wherein the outermost layer contains at least one species of resin selected from the group consisting of polyurea, polyurethane, polyamide, polyester, nylon and epoxy polymer.
18. The hollow resin particle according to claim 12 , which contains a resin crosslinked by an inorganic component.
19. A composition comprising the hollow resin particle according to claim 12 .
20. A composition comprising the hollow resin particle according to claim 14 .
21. The method according to claim 1 , wherein the lipophilic reaction component A is a polyisocyanate and the hydrophilic reaction component B is at least one species selected from the group consisting of water, amine, polyol, and polycarboxylic acid.
22. The method according to claim 1 , wherein the lipophilic reaction component A is an epoxy prepolymer and the hydrophilic reaction component B is an amine and/or a polycarboxylic acid.
23. The method according to claim 1 , wherein the lipophilic reaction component A is an acid halide and the hydrophilic reaction component B is an amine or polyol.
24. The method according to claim 2 , wherein the lipophilic reaction component A is a polyisocyanate and the hydrophilic reaction component B is at least one species selected from the group consisting of water, amine, polyol, and polycarboxylic acid.
25. The method according to claim 2 , wherein the lipophilic reaction component A is an epoxy prepolymer and the hydrophilic reaction component B is an amine and/or a polycarboxylic acid.
26. The method according to claim 2 , wherein the lipophilic reaction component A is an acid halide and the hydrophilic reaction component B is an amine or polyol.