Calcium carbonate granulation
Highly compactable granulations and methods for preparing highly compactable granulations are disclosed. More particularly, highly compactable calcium carbonate granulations are disclosed. The granulations comprise powdered materials such as calcium carbonate that have small median particle sizes. The disclosed granulations are useful in pharmaceutical and nutraceutical tableting and provide smaller tablet sizes upon compression than previously available.
1. A wet granulation process for preparing calcium carbonate granulation comprising the steps of:
(1) mixing in a high shear mixer a composition comprising powdered calcium carbonate having a median particle diameter from 6 μm to 12 μm, maltodextrin and optionally additional excipients;
(2) adding water to the composition in an amount from about 5 to about 20% by weight based on the amount of calcium carbonate and mixing therewith;
(3) adding oil to the composition and mixing therewith; and
(4) drying the resulting composition by convection drying in a horizontal fluidized bed oven to thereby provide a calcium carbonate granulation.
2. The process according to claim 1 , wherein said calcium carbonate powder has a median particle size of 12 μm.
3. The process according to claim 1 , wherein said granulation has a tap density between about 1.0 and about 2.0 g/cm 3 .
4. The process according to claim 2 , wherein said granulation has a tap density between about 1.1 and about 2.0 g/cm 3 .
5. The process according to claim 1 , wherein said maltodextrin comprises from about 2% to about 10% by weight of said granulation.
6. The process according to claim 2 , wherein said oil comprises from about 0.1% to about 1% by weight of said granulation.
7. The process according to claim 1 , further comprising one or more excipients selected from the group consisting of diluents, binders, glidants, lubricants, disintegrants, colors, flavors, sweeteners, solubility retarding agents, and combinations thereof.
8. The process according to claim 1 , wherein said granulation has a water content of less than about 1% by weight.
9. The process according to claim 2 , wherein said calcium carbonate powder has a particle size distribution wherein at least 50% of the bulk volume of the powder has a particle size between 4 and 20 μm and at least 30% of the bulk volume of the powder has a particle size between 8 and 16 μm.
10. The process according to claim 2 , wherein said calcium Carbonate powder has a particle size distribution broader than a distribution wherein at least 50% or more of the bulk volume of the powder has a particle size between 4 and 20 μm and at least 30% of the bulk volume of the powder has a particle size between 8 and 16 μm.