Granules of powdery mineral and method for production of granules
The present application relates to granules of powdery mineral particles produced by spray granulation of a liquid slurry comprising powdery minerals particles having particle size below 10 m, at least one water-reducing agent and/or at least one binder agent and/or at least one dispersing agent. The application further relates to a method for producing such granules.
1. Granules of powdery manganomanganic oxide particles produced by spray granulation of a liquid slurry comprising powdery manganomanganic oxide particles having particle size below 10 μm, at least one water-reducing agent and/or at least one binder agent and/or at least one dispersing agent where the total amount of agents in the liquid slurry is between is between 0.05 and 1.5% by weight based on the weight of manganomanganic oxide particles and where said granules have a water content between 0.1 and 0.5% by weight.
2. Granules according to claim 1 , wherein the granules have a water content of between 0.2 and 0.4% by weight.
3. Granules according to claim 1 , wherein the granules are made from a liquid slurry containing 5-35% by weight of water.
4. Granules according to claim 1 , wherein the water-reducing agent is selected among naphthalene-sulfonate, lignosulfonate, melamine, acrylic polymers and hexametaphosphate.
5. Granules according to claim 1 , wherein the binder agent is selected among ammonium lignosulfonate, dextran, sugar, polymethacrylate, polyvinyl alcohol, polyethylene, metakaolin water-glass, hexametaphosphate, lignosulfonate and naphthalene-sulfonate.
6. Granules according to claim 1 , wherein the dispersing agent is selected among sodium capryloiminodipropionate, tridecyl alcohol ethoxylate, alkyl naphthalene sulfate sodium salt, hexametaphosphate, lignosulfonate, acryl polymers, melamine and naphthalene sulfonate.
7. Granules according to claim 1 , wherein the water reducing agent is sodium lignosulfonate and/or calcium lignosulfonate, the binder agent is calcium sulfonate and/or sodium lignosulfonate and the dispersing agent is calcium lignosulfonate and/or sodium lignosulfonate.
8. A method for producing spray dried granules of manganomanganic particles having a particle size below 10 microns, comprising the steps of spray drying a liquid slurry containing manganomanganic oxide particles, wherein the liquid slurry contains 5-35% by weight of water and at least one water-reducing agent, and/or at least one binder agent and/or at least one dispersing agent, where said slurry is supplied to a spray drying apparatus and spray dried by supplying hot air to provide spray dried granules having a water content of between 0.1 and 0.5% by weight.
9. Method according to claim 8 , wherein the liquid slurry is subjected to wet screening before being supplied to the spray drying apparatus.