Nanoparticle implantation
A method for forming a coating of nano-sized material on the surface of another material using a micromachining bead-blasting machine for implantation of nanoparticles is disclosed. The method can be practiced with a wide range of target materials, nanoparticles (such as carbon-nanotubes, CNTs), and environmental conditions, using a wide range of carrier bead sizes and materials, or without carrier beads. The claimed implantation method can be used to fabricate a surface-activated CNT-cathode for use in a field emission device. The implantation method can also be used for chemically reacting any of the materials present near the point of impact with each other.
1. A method for altering properties of a surface, comprising the steps of:
providing a target surface for alteration; and
performing an implantation of nanoparticles into the target surface, wherein:
said implantation is performed with a bead-blasting process using carrier beads, such that the carrier beads strike the target surface; and
mixing said nanoparticles with said carrier beads before performing said implantation, such that said nanoparticles become physically attached to said carrier beads.
2. The method as recited in claim 1 , further comprising:
a chemical reaction of said nanoparticles with said target surface upon said implantation.
3. The method as recited in claim 1 , wherein said target surface after said implantation with said nanoparticles is used as a cathode in a field emission device to extract electrons.
4. The method as recited in claim 3 , wherein said field emission device, is configured with a. cathodoluminescent anode to emit light as a result of an electric field between said cathode and said anode.
5. The method as recited in claim 1 , wherein said implantation deforms said target surface.
6. The method as recited in claim 5 , wherein said implantation plastically deforms said target surface.
7. The method as recited in claim 1 , wherein said nanoparticles are physically attached to said carrier beads by van der Waals forces.
8. The method as recited in claim 1 , wherein said nanoparticles comprise carbon nanotubes.
9. The method as recited in claim 1 , wherein a portion of said carrier beads are not retained by said target surface after said implantation.
10. The method as recited in claim 1 , wherein an adhesive coating is applied to said carrier beads before mixing with said nanoparticles.
11. The method as recited in claim 1 , wherein the carrier beads comprise a material that transitions from a solid to a fluid at room temperature.
12. A method for altering surface properties of particles, comprising the steps of
providing a target surface;
mixing nanoparticles with said particles, such that said nanoparticles become physically attached to said particles; and
performing an implantation of said nanoparticles into the surface of said particles using a blasting process such. that said particles strike the target surface.
13. The method recited in claim 12 , wherein the target surface is harder than said particles.
14. The method as recited in. claim 12 , further comprising:
a chemical reaction of said nanoparticles with said particles upon said implantation.
15. The method as recited in claim 12 , wherein:
the nanoparticles comprise alumina; and
the particles comprise a polymer.
16. The method as recited in claim 12 , wherein said nanoparticles have a higher melting point than said particles.
17. The method as recited in claim 12 , wherein said. particles are not retained by the target surface.