The invention relates to polyvinlyl alcohol gels which are suitable for use in the organism and which are formed at the site of application (in situ) from a viscous liquid by partial crystallization and network formation.
1. An injectable polyvinyl alcohol gel, characterized in that
a) the gel comprises polyvinyl alcohol and water and is formed from a solution at 0 to 100° C.; and
b) the gel comprises at least one polyvinyl alcohol PVA1, and at least one polyvinyl alcohol PVA2; and
c) the polymerization degree DPn of PVA1 is >1000; and
d) the polymerization degree DPn of PVA2 ranges from 50 to 1000; and
e) the hydrolysis degree of PVA1 and PVA2 in mol. % is >98.
2. The injectable polyvinyl alcohol gel according to claim 1 , characterized in that the hydrolysis degree of PVA2 in mol. % is >99.85.
3. The injectable polyvinyl alcohol gel according to claim 2 , characterized in that the hydrolysis degree of PVA1 in mol. % is >99.85.
4. The injectable polyvinyl alcohol gel according to claim 1 , characterized in that the smallest macromolecules of the molecular distributions of PVA1 and PVA2 have a polymerization degree of >40.
5. The injectable polyvinyl alcohol gel according to claim 1 , characterized in that gel formation takes place in the body temperature range under in situ conditions.
6. The injectable polyvinyl alcohol gel according to claim 1 , characterized in that the gel has a modulus of elasticity ranging from 0.1 to 25 MPa at room temperature in at least one of compression and in the tensile test.
7. The injectable polyvinyl alcohol gel according to claim 1 , characterized in that the gel has at least 10% of at least one of the modulus of elasticity and the strength of the cured state after 1 h.
8. The injectable polyvinyl alcohol gel according to claim 1 , characterized in that a film of 0.5 mm thickness swelled in distilled water at room temperature has a polymer loss in % after 14 days of <7.
9. The injectable polyvinyl alcohol gel according to claim 1 , characterized in that the gel comprises at least one filler, and/or at least one additional polymer selected from the group consisting of polycarbonates, polyacrylates, polymethacrylates. polyethylene glycols, polyethylene oxide, polyvinyl pyrrolidone, polycaprolactone, hydrocolloids, and polysaccharides.
10. A method for carrying out a procedure in the area of biomedicine, tissue and scaffold engineering, orthopedics and plastic surgery wherein the procedure utilizes a previous gel, the method comprising the step of replacing the previous gel with an injectable polyvinyl alcohol gel according to claim 1 .
11. A method for replacement and repair of intervertabral discs which utilizes the polyvinyl alcohol gel according to claim 1 .
12. The injectable polyvinyl alcohol gel according to claim 1 , characterized in that the hydrolysis degree of PVA2 in mol. % is >99.9.
13. The injectable polyvinyl alcohol gel according to claim 1 , characterized in that the hydrolysis degree of PVA2 in mol. % is >99.95.
14. The injectable polyvinyl alcohol gel according to claim 1 , characterized in that the hydrolysis degree of PVA2 in mol. % is >99.98.
15. The injectable polyvinyl alcohol gel according to claim 1 , characterized in that a film of roughly 0.5 mm thickness swelled in distilled water at room temperature has a polymer loss in % after 14 days of <3.