Dental polymerizable core build-up material of separately packed type
The invention provides a divided type dental polymeric core build-up material including a first paste (A) and a second paste (B), in which each of the pastes is a paste obtained by mixing at least a (meth)acrylate monomer, a filler having a particle size distribution within a range of 0.1 through 40 μm and an average particle diameter of 0.7 through 10 μm, and a fine particle filler having an average particle diameter of primary particles of 0.001 through 0.050 μm, and having a viscosity at 25° C. of 280 through 470 P, and in which one of the pastes includes an oxidant and the other includes a reductant and at least one of the pastes includes a photopolymerization catalyst. The divided type dental polymeric core build-up material of this invention has high operability in core build-up and forms a polymerically cured substance with a good mechanical property.
1. A divided dental polymeric core build-up material comprising a first paste (A) and a second paste (B),
wherein each of said first paste (A) and said second paste (B) is a paste that includes a (meth)acrylate monomer (I), and a filler composition consisting essentially of a first and second filler, wherein the first filler (II) has a particle size distribution within a range of 0.1 through 40 μm and an average particle diameter of 0.7 through 10 μm and is present in an amount of 190 to 370 parts by weight based on 100 parts by weight of the (meth)acrylate monomer (I), and the second-filler (III) has an average particle diameter of primary particles of 0.005 through 0.045 μm in an amount of 3 to 60 parts by weight based on 100 parts by weight of the (meth)acrylate monomer (I), and has a viscosity at 25° C. of 280 through 470 P,
one of said first paste (A) and said second paste (B) includes an oxidant (IV) and the other includes a reductant (V), and
at least one of said first paste (A) and said second paste (B) includes a photopolymerization catalyst (VI).
2. A divided dental polymeric core build-up material comprising a first paste (B) and a second paste (B),
wherein each of said first paste (A) and said second paste (B) is a paste that is obtained by mixing at least a (meth)acrylate monomer (I), and a filler composition consisting essentially of a first and second filler, wherein the first filler (II) has a particle size distribution within a range of 0.1 through 40 μm and an average particle diameter of 0.7 through 10 μm in an amount of 190 to 370 parts by weight based on 100 parts by weight of the (meth)acrylate monomer (I), and the second filler (III) has an average particle diameter of primary particles of 0.005 through 0.045 μm in an amount of 3 to 60 parts by weight based on 100 parts by weight of the (meth)acrylate monomer (I), and has a viscosity at 25° C. of 280 through 470 P,
one of said first paste (A) and said second paste (B) includes an oxidant (IV) and the other includes a reductant (V), and
at least one of said first paste (A) and said second paste (B) includes a photopolymerization catalyst (VI).
3. The divided dental polymeric core build-up material according to claim 2 ,
wherein said filler (II) has a particle size distribution within a range of 0.5 through 30 μm and an average particle diameter of 0.7 through 10 μm.
4. The divided dental polymeric core build-up material according to claim 2 ,
wherein said filler (II) has a particle size distribution within a range of 0.5 through 30 μm and an average particle diameter of 1.5 through 10 μm.
5. The divided type dental polymeric core build-up material according to claim 2 ,
wherein a mixture of said first paste (A) and said second paste (B) has a viscosity at 25° C. of 280 through 470 P.
6. The divided dental polymeric core build-up material according to claim 2 ,
wherein both of said first paste (A) and said second paste (B) include said photopolymerization catalyst (VI).
7. The divided dental polymeric core build-up material according to claim 6 ,
wherein ratios of said oxidant (IV) and said photopolymerization catalyst (VI) included in said first paste (A) are 0.01 through 5 parts by weight and 0.01 through 5 parts by weight based on 100 parts by weight of the (meth)acrylate monomer (I) included in said first paste (A), and
ratios of said reductant (V) and said photopolymerization catalyst (VI) included in said second paste (B) are 0.01 through 5 parts by weight and 0.01 through 5 parts by weight based on 100 parts by weight of the (meth)acrylate monomer (I) included in said second paste (B).
8. The divided dental polymeric core build-up material according to claim 7 ,
wherein a weight ratio between said first paste (A) and said second paste (B) is 1:2 through 2:1.
9. The divided dental polymeric core build-up material according to claim 3 , wherein a mixture of said first paste (A) and said second paste (B) has a viscosity at 25° C. of 280 through 470 P.
10. The divided dental polymeric core build-up material according to claim 4 , wherein a mixture of said first paste (A) and said second paste (B) has a viscosity at 25° C. of 280 through 470 P.
11. The divided dental polymeric core build-up material according to claim 3 , wherein both of said first paste (A) and said second paste (B) include said photopolymerization catalyst (VI).
12. The divided dental polymeric core build-up material according to claim 4 , wherein both of said first paste (A) and said second paste (B) include said photopolymerization catalyst (VI).
13. The divided dental polymeric core build-up material according to claim 5 , wherein both of said first paste (A) and said second paste (B) include said photopolymerization catalyst (VI).
14. The divided dental polymeric core build-up material according to claim 9 , wherein both of said first paste (A) and said second paste (B) include said photopolymerization catalyst (VI).
15. The divided dental polymeric core build-up material according to claim 10 , wherein both of said first paste (A) and said second paste (B) include said photopolymerization catalyst (VI).