Tungstic acid powder consisting of spherical tungsten particles and method for producing same
Process for the production of a powdered spherical tungstic acid by acidification of an aqueous alkaline tungstate solution with mineral acid at elevated temperature, preferably in a continuous stirred tank or a cascade of at least 2 continuous stirred tanks, and tungstic acid obtainable in this way, which is characterized by a high bulk density and spherical morphology.
1. A process for the production of a powdered tungstic acid having a spherical morphology which comprises reacting an aqueous alkaline tungstate solution with a mineral acid at a temperature of 50 to 103° C., wherein the reaction is performed continuously in a continuous stirred tank or a cascade of at least two continuous stirred tanks and wherein the reaction of the alkaline tungstate solution with the mineral acid is performed at a molar ratio of mineral acid to tungsten of 9:1 to 4:1 and wherein at least 95% of the powder particles display a ratio of diameter of a larger circle to diameter of a smaller circle of 1.0 to 1.4.
2. The process according to claim 1 , wherein the reaction takes place at a temperature of 70 to 100° C.
3. The process according to claim 1 , wherein the alkaline tungstate solution is an aqueous sodium tungstate solution.
4. The process according to claim 1 , wherein the mineral acid is an aqueous sulfuric acid having a content of H 2 SO 4 of 50 to 70 wt. %.
5. The process according to claim 1 , wherein the residence time in the reaction chamber is 4 to 6 h.
6. The process according to claim 2 , wherein the alkaline tungstate solution is an aqueous sodium tungstate solution.
7. The process according to claim 6 , wherein the mineral acid is an aqueous sulfuric acid having a content of H 2 SO 4 of 50 to 70 wt. %.
8. The process according to claim 7 , wherein the residence time in the reaction chamber is 4 to 6 h.
9. The process according to claim 1 , which consists essentially of reacting an aqueous alkaline tungstate solution with a mineral acid at a temperature of 50 to 103° C., wherein the reaction is performed continuously in a continuous stirred tank or a cascade of at least two continuous stirred tanks.
10. The process according to claim 1 , which consists of reacting an aqueous alkaline tungstate solution with a mineral acid at a temperature of 50 to 103° C., wherein the reaction is performed continuously in a continuous stirred tank or a cascade of at least two continuous stirred tanks.
11. The process according to claim 1 , wherein the reaction takes place at a temperature of 75 to 100° C.
12. The process according to claim 8 , wherein the reaction takes place at a temperature of 75 to 95° C.