Method of cleaning carbon composite prior to application of thermal coating
A method of cleaning a carbon work piece includes the step of applying an acetone cleaning agent to the carbon work piece to remove debris therefrom. The removal of debris promotes adhesion between the carbon work piece and a subsequently applied coating. For example, other steps may precede the acetone cleaning step, such as submersing the carbon work piece in deionized water. In one example, a subsequent coating process deposits an alumina coating on the carbon work piece.
1. A method of cleaning a carbon composite seal member, comprising:
(a) soaking the carbon composite seal member in deionized water;
(b) removing the carbon composite seal member from the deionized water and brushing the carbon composite seal member to remove air bubbles therefrom;
(c) applying an acetone cleaning agent to the carbon composite seal member to remove debris therefrom;
(d) depositing a coating on the carbon composite seal member and
(e) reusing the acetone cleaning agent to clean subsequent carbon composite seal members and establishing a threshold contamination level of the acetone cleaning agent based upon a measured characteristic of the acetone cleaning agent wherein said characteristic includes rejecting use of said acetone cleaning agent if a specific gravity of said acetone cleaning agent is above about 0.87.
2. The method as recited in claim 1 , wherein said step (b) includes completely submerging the carbon composite seal member in a container holding the acetone cleaning agent.
3. The method as recited in claim 1 , further comprising:
(f) blowing ambient air over the carbon composite seal member to remove the acetone cleaning agent from the carbon composite seal member after said step (c).
4. A method of cleaning a carbon composite seal member, comprising:
(a) applying an acetone cleaning agent to the carbon composite seal member to remove debris from pores of the carbon composite seal member, and
(b) reusing the acetone cleaning agent to clean subsequent carbon composite seal members and
(c) establishing a threshold contamination level of the acetone cleaning agent based upon a measured characteristic of the acetone cleaning agent wherein said characteristic includes rejecting use of said acetone cleaning agent if a specific gravity of said acetone cleaning agent is above about 0.87,
further comprising:
(d) soaking the carbon composite seal member in deionized water before step (a).
5. The method as recited in claim 4 , further comprising:
(e) removing the carbon composite seal member from the deionized water and brushing the carbon composite seal member to remove air bubbles therefrom before said step (a).
6. The method as recited in claim 5 , further comprising:
(f) blowing ambient air over the carbon composite seal member to remove the deionized water therefrom.