Nano glass powder and use thereof, in particular multicomponent glass powder with a mean particle size of less than 1 μm
A glass powder or a glass-ceramic powder is provided that includes multicomponent glasses with at least three elements, where the glass powder or a glass-ceramic powder has a mean particle size of less than 1 μm. In some embodiments, the mean particle size is less than 0.1 μm, while in other embodiments the mean particle size is less than 10 nm.
1. A method of manufacturing a multi-component glass or glass ceramic powder in the form of nanoparticles, comprising:
providing at least three initial glass forming materials;
vaporizing all of the initial glass forming materials in a plasma to form vaporized components; and
depositing the vaporized components on a substrate so that the vaporized components are organized in a vitreous state or in an amorphous form, which has a composition comprising 5 to 55 weight percent based on oxide of P 2 O 5 , 20 to 35 weight percent based on oxide of ZnO, and at least one initial glass forming material selected from the group consisting of 0.1 to 25 weight percent based on oxide of Na 2 O, 2.5 weight percent based on oxide of Li 2 O, 2 to 2.6 weight percent based on oxide of K 2 O, and 1 to 11.8 weight percent based on oxide of Al 2 O 3 .
2. The method according to claim 1 , wherein the step of providing at least three initial glass forming materials comprises providing glasses that are already multi-component glasses with particle sizes of less than 1 μm.
3. The method according claim 1 , wherein the multi-component glass or glass ceramic powder has a mean particle size of less than 200 nm.
4. The method according to claim 1 , wherein the multi-component glass or glass ceramic powder comprises particles having a surface area that is larger than 50 m 2 /g as determined by the BET method.
5. A method of manufacturing a multi-component glass or glass ceramic powder in the form of nanoparticles, comprising:
providing at least three initial glass forming materials;
vaporizing all of the initial glass forming materials in a plasma to form vaporized components; and
depositing the vaporized components on a substrate so that the vaporized components are organized in a vitreous state or in an amorphous form, which has a composition comprising 10 to 50 weight percent based on oxide of B 2 O 3 , 5 to 80 weight percent based on oxide of SiO 2 , and PbO.
6. The method according to claim 5 , wherein the sum of SiO 2 +B 2 O 3 +P 2 O 5 is more than 25 weight percent.
7. The method according to claim 5 , wherein the step of providing at least three initial glass forming materials comprises providing glasses that are already multi-component glasses with particle sizes of less than 1 μm.
8. The method according claim 5 , wherein the multi-component glass or glass ceramic powder has a mean particle size of less than 200 nm.
9. The method according to claim 5 , wherein the multi-component glass or glass ceramic powder comprises particles having a surface area that is larger than 50 m 2 /g as determined by the BET method.
10. The method according to claim 5 , wherein the composition comprises 40 to 80 weight percent based on oxide of SiO 2 and 13.4 to 50 weight percent based on oxide of B 2 O 3 .