Peelable composite thermoplastic sealants in packaging films
View Patent ↗A peelable sealing structure includes a sealing layer and one or more optional additional layers. The peelable sealing structure includes a sealing surface that is formable into a peelable seal upon contact with a sealing substrate at all temperatures in a peelable seal temperature range. Moreover, the peelable sealing structure comprises a thermoplastic polymer and an additive dispersed within at least a portion of the thermoplastic polymer with the peelable sealing structure defining the sealing surface.
1. A peelable sealing structure comprising:
a thermoplastic polymer; and
an exfoliated organoclay dispersed within at least a portion of the thermoplastic polymer, wherein the peelable sealing structure includes a sealing layer that defines a sealing surface, the sealing surface formable into a peelable seal at all temperatures within a peelable seal temperature range, the peelable seal temperature range being from a seal initiation temperature to a temperature that is at least 100 F. degrees above the seal initiation temperature wherein the seal initiation temperature is from about 170° F. to about 350° F. and the organoclay comprises platelets having an average separation of at least 20 angstroms, the sealing surface having a roughness average from about 1500 to about 5000 angstroms and the sealing layer having a tensile modulus from about 500 to about 2000 MPa.
2. The peelable sealing structure of claim 1 wherein the organoclay comprises a plurality of particles having a spatial dimension less than 200 nm.
3. The peelable sealing structure of claim 1 wherein the organoclay comprises a clay selected from the group consisting of kaolinite, montmorillonite-smectite clays, bentonite clays, illite clays, and combinations thereof.
4. The peelable sealing structure of claim 1 wherein the organoclay is present in an amount from 1 wt % to 20 wt % of the combined weight of the thermoplastic polymer and the organoclay.
5. The peelable sealing structure of claim 1 wherein the organoclay is present in an amount from 2 wt % to 10 wt % of the combined weight of the thermoplastic polymer and the organoclay.
6. The peelable sealing structure of claim 1 wherein the thermoplastic polymer comprises a component selected from the group consisting of nylons, polyolefins, polystyrenes, polyesters, polycarbonates, copolymers of ethylene, copolymers of propylene, ethylene vinyl acetate, and mixtures thereof.
7. The peelable sealing structure of claim 1 wherein the thermoplastic polymer comprises a component selected from the group consisting of ethylene acrylic acid, ethylene ethyl acrylate, ethylene ionomers, and combinations thereof.
8. The peelable sealing structure of claim 1 wherein the thermoplastic polymer comprises ethylene vinyl acetate.
9. The peelable sealing structure of claim 1 wherein the organoclay has a surface area greater than 100 m 2 /gram and an aspect ratio greater than 10, wherein the peelable sealing structure defines a sealing surface.
10. The peelable sealing structure of claim 1 wherein the thermoplastic polymer comprises a polyolefin.
11. The peelable sealing structure of claim 1 wherein the thermoplastic polymer comprises a component selected from the group consisting of copolymers of ethylene, copolymers of propylene, and mixtures thereof.