Methods for preparing coated metal substrates
A coated metal substrate useful for carrying an exhaust emission treatment catalyst such as a three-way conversion catalyst for use with small engine platforms. The coated metal substrate comprises a metal such as a stainless steel, a carbon steel, a FeCr alloy, HASTELLOY® and the like. The coating on the metal substrate comprises an alumina silicate having alumina particles impregnated therein. The coating is applied using a liquid dispersion containing an aluminum silicate and the alumina particles are dispersed into the aluminum silicate coating while the coating is still wet. The coated metal substrate is then calcined. Thereafter, a washcoat containing an engine exhaust treatment catalyst may be applied to the surface of the coated metal substrate.
1. A method for preparing a coated metal substrate for use in the catalytic reduction of engine exhaust emissions comprising the steps of:
(a) cleaning the surface of a metal substrate;
(b) coating the metal substrate with a liquid dispersion containing an aluminum silicate;
(c) impregnating the coated metal substrate resulting from step (b) with alumina particles having a particle size in the range of about 5 to about 15 microns, while the aluminum silicate coating on the metal substrate is still wet; and
(d) calcining the coated metal substrate resulting from step (c).
2. The method of claim 1 wherein step (d) is carried out at a temperature of about 350 to about 550° C. for about 0.25 to about 2 hours.
3. The method of claim 1 further comprising applying a washcoat comprising an engine exhaust treatment catalyst to the coated metal substrate resulting from step (d).
4. The method of claim 3 wherein the catalyst comprises a three-way conversion catalyst.
5. The method of claim 3 , wherein the washcoat is applied to the coated metal substrate using a method selected from spraying, dipping or rolling.
6. The method of claim 3 , further comprising air drying the coated metal substrate at about 60° C. to about 100° C. for about 0.5 to about 2 hours, after applying the washcoat.
7. The method of claim 6 , further comprising the step of calcining the coated metal substrate at a temperature of about 350° C. to about 550° C. for about 0.25 to about 2 hours after air drying the coated metal substrate.
8. The method of claim 1 wherein the metal substrate comprises a metal selected from the group consisting of a stainless steel, a carbon steel, titanium, a FeCr alloy and a metal alloy containing nickel, chromium and molybdenum.
9. The method of claim 8 wherein the metal substrate comprises a stainless steel.
10. The method of claim 1 wherein the alumina particles have a particle size in the range of 6 to 9 microns.
11. The method of claim 1 wherein the alumina particles are present in an amount of about 0.01 to about 0.5 g/in 2 of the aluminum silicate coating.
12. The method of claim 1 wherein the liquid dispersion comprises the following components in the indicated amounts:
component
amount, wt. %
sodium potassium aluminum silicate
about 40 to about 45
water
about 35 to about 40
acrylic copolymer
about 1 to about 5
chromia titania frit
about 1 to about 5
aluminum oxide
about 1 to about 5
potassium hydroxide
about 1 to about 5
amorphous silica
about 1 to about 5
cobalt oxide
about 1 to about 5
13. The method of claim 1 wherein the liquid dispersion comprises the following components in the indicated amounts:
component
amount, wt. %
silicon carbide
about 45 to about 50
water
about 20 to about 26
aluminum phosphate
about 10 to about 15
amorphous silicon oxide binders
about 2 to about 6
boric acid
about 1 to about 3
ethyl alcohol
about 3 to about 7
mullite
about 4 to about 6
14. The method of claim 1 , wherein the liquid dispersion is applied to the metal substrate using a method selected from dipping, brushing, sponge roller, or air gun spraying.
15. The method of claim 1 , wherein the alumina particles are impregnated to the coated metal using a method selected from dipping or brushing.
16. A method for preparing a coated metal substrate for use in the catalytic reduction of engine exhaust emissions comprising the steps of:
(a) cleaning the surface of a metal substrate, wherein the metal substrate is employed in the form of an expansion cone or exhaust gas silencer;
(b) coating the metal substrate with a liquid dispersion containing an aluminum silicate;
(c) impregnating the coated metal substrate resulting from step (b) with alumina particles having a particle size in the range of about 5 to about 15 microns, while the aluminum silicate coating on the metal substrate is still wet; and
(d) calcining the coated metal substrate resulting from step (c).
17. The method of claim 16 wherein the expansion cone has a length of about 200 to about 300 mm, a diameter ranging from about 30 to about 100 mm, a thickness of about 0.5 to about 3 mm and an inside surface area of about 0.03 to about 0.06 m 2 .
18. The method of claim 17 , wherein the expansion cone has a length of about 100 mm to 300 mm.
19. The method of claim 16 further comprising applying a washcoat comprising an engine exhaust treatment catalyst to the coated metal substrate resulting from step (d).
20. The method of claim 19 wherein the catalyst comprises a three-way conversion catalyst.