Curing binder material for carbon nanotube electron emission cathodes
A binder material, inorganic polymer, is used to formulate carbon nanotube pastes. This material can be cured at 200° C. and has a thermal-stability up to 500° C. Low-out gassing of this binder material makes it a good candidate for long life field emission devices. Due to better adhesion with this binder material, a strong adhesive peelable polymer from liquid form can be applied on the CNT cathode to achieve a uniform activation with even contact and pressure on the surface. The peelable polymer films may be used both as an activation layer and a mask layer to fabricate high-resolution patterned carbon nanotube cathodes for field emission devices using lithographic processes.
1. A composite for a field emission cathode, comprising an inorganic polymer mixed with carbon nanotubes wherein the inorganic polymer is a silicon-containing, ladder-like polymer.
2. The composite of claim 1 , wherein the inorganic polymer is polyphenylsilsesquioxane (PPSQ).
3. The composite of claim 1 , wherein the inorganic polymer is a polyhedral oligomeric silsesquioxane (POSS).
4. A composite comprising a mixture of carbon nanotubes, graphite powder and an inorganic polymer, wherein the inorganic polymer is a silicon-containing, ladder-like polymer.
5. A field emission cathode comprising:
a substrate;
a field emitter on the substrate wherein the field emitter comprises a paste comprising carbon nanotubes and an inorganic polymer, wherein the inorganic polymer is a silicon-containing, ladder-like polymer; and
circuitry for producing an electric field to cause a field emission of electrons from the field emitter.
6. The field emission cathode of claim 5 , wherein the inorganic polymer comprises PPSQ.
7. The field emission cathode of claim 5 , wherein the inorganic polymer comprises POSS.
8. The field emission cathode of claim 5 , wherein the cathode is configured to be activated by forming a film from a liquid polymer solution over the cathode, followed by peeling the film off the cathode.
9. A field emission cathode comprising:
a substrate;
a field emitter on the substrate wherein the field emitter comprises a paste comprising carbon nanotubes and an inorganic polymer; and
circuitry for producing an electric field to cause a field emission of electrons from the field emitter, wherein the cathode is configured to be activated by forming a film from a liquid polymer solution over the cathode, followed by peeling the film off the cathode, wherein the cathode is configured to have an emission current that increases from about 5 mA at an electric field of about 2.4 (V/ium) to about 30 mA at an electric field of about 3.5 (V/ium).
10. A field emission cathode comprising:
a substrate;
a field emitter on the substrate wherein the field emitter comprises a paste comprising carbon nanotubes and an inorganic powder, the inorganic powder comprises a silicon containing, ladder-like polymer; and circuitry for producing an electric field to cause a field emission of electrons from the field emitter.
11. The field emission cathode of claim 10 , wherein the inorganic powder comprises PPSQ.
12. The field emission cathode of claim 10 , wherein the inorganic powder comprises POSS.
13. The field emission cathode of claim 10 , wherein the field emitter is configured to be activated by forming a film from a liquid polymer solution over the field emitter, followed by peeling the film off the field emitter.
14. A field emission cathode comprising:
a substrate;
a field emitter on the substrate wherein the field emitter comprises a paste comprising carbon nanotubes and an inorganic powder; and
circuitry for producing an electric field to cause a field emission of electrons from the field emitter, wherein the field emission cathode is configured to have an emission current that increases from about 5 mA at an electric field of about 2.4 (V/ium) to about 30 mA at an electric field of about 3.5 (V/ium).