Dental prosthesis method and alloys
Dental prostheses are fabricated as a metallic alloy body by a technique that produces scrap alloy. Suitable gold base alloys have only base metal alloying additions which are more readily oxidized than gold and when combined with the gold can be age hardened. Exemplary metals include titanium, zirconium, yttrium and chromium. Scrap from fabricating a dental prosthesis is melted in air so that the base metals are all oxidized and substantially pure gold is reclaimed for reuse in new alloys.
1. A process for forming a dental prosthesis comprising the steps of:
(i) providing a metallic alloy comprising principally gold with additions of at least one additional metal selected from the group consisting of:
from 1 to 5% by weight of titanium, zirconium or a combination thereof,
from 0.25 to 2% by weight yttrium, and
from 1 to 10% by weight chromium;
and a grain refiner that oxidizes more readily than gold provided that the grain refiner is not a platinum group metal; and
(ii) forming a dental prosthesis from said metallic alloy, wherein said forming step comprises at least one process selected from the group consisting of machining a dental prosthesis from an alloy body formed from said metallic alloy, and forming a dental prosthesis directly by energy beam sintering of a powder formed from the metallic alloy.
2. A process according to claim 1 wherein the grain refiner is selected from the group consisting of barium, boron and grain refining rare earth metal, in an amount of up to 0.3% by weight of the alloy.
3. A process according to claim 2 wherein the at least one additional metal comprises from 1 to 5% by weight titanium.
4. A process according to claim 1 wherein the at least one additional metal comprises from 1 to 5% by weight titanium.
5. A process according to claim 1 wherein the at least one additional metal comprises at least 0.5% by weight titanium and at least 0.5% by weight zirconium, the total of titanium and zirconium being in the range of from 1 to 5% of the alloy by weight.
6. A process according to claim 1 wherein the at least one additional metal comprises from 1 to 5% by weight zirconium.
7. A process according to claim 1 wherein the at least one additional metal comprises from 0.25 to 2% by weight yttrium.
8. A process according to claim 1 wherein the at least one additional metal comprises from 1 to 10% by weight chromium.
9. A process according to claim 1 further comprising the step of:
accumulating scrap metal from the forming step; and
oxidizing the scrap to recover substantially pure gold.
10. A process according to claim 1 wherein the at least one additional metal is selected from the group consisting of from 1 to 5% by weight of zirconium, from 0.25 to 2% by weight yttrium, and from 1 to 10% by weight chromium.