Aminoplast resin composition
Resin compositions, methods of forming such resin compositions, methods of using such resin compositions and substrates treated with such resin compositions are disclosed. One of such resin compositions contains no formaldehyde and is useful as a binder. Such resin composition comprises the reaction product of: a—melamine, b—at least one aldehyde of formula (1) as defined in the specification, c—a cross linking agent, wherein the cross linking agent is glyoxylic acid, and d—at least one polyol having 2 or more than 2 hydroxyl groups. The resin composition of the present invention can provide performance characteristics to which they are applied.
1. A process for binding a substrate comprising the steps of applying a resin composition to a substrate and curing the resin composition, wherein the resin composition comprises the reaction product of;
a—melamine,
b—at least one aldehyde of formula (1),
R—CHO (1)
in which R is a dialkoxymethyl group, a 1,3-dioxolane-2-yl group optionally substituted on the vertex 4 and/or 5 by one or more alkyl groups or a 1,3-dioxan-2-yl group optionally substituted on its vertices 4 , 5 and/or 6 by one or more alkyl groups,
c—a cross linking agent, wherein the crossing linking agent is glyoxylic acid,
d—at least one polyol having 2 or more than 2 hydroxyl groups.
2. The process according to claim 1 , wherein the curing step further comprises heating the resin composition.
3. A substrate made in accordance with the process of claim 1 .
4. The substrate according to claim 3 , wherein the substrate is selected from the group consisting of cellulosic, fiberglass, polymeric materials and composite blends thereof.
5. The substrate according to claim 3 , wherein the substrate is selected from the group consisting of polyester, nylon and cellulosic substrates.
6. A process for binding a substrate comprising the steps of applying a resin composition to a substrate and curing the resin composition, wherein the resin composition is made by a process including the steps of condensing, under agitation, a melamine and at least one aldehyde of
R—CHO formula (1)
in which R is a dialkoxymethyl group, a 1,3-dioxolan-2-yl group optionally substituted on the vertex 4 and/or 5 by one or more alkyl groups or a 1,3-dioxan-2-yl group optionally substituted on its vertices 4 , 5 and/or 6 by one or more alkyl groups, in aqueous solution and in the presence of an alkaline catalyst, at a basic pH between about 8 and about 10 and at a temperature between about 20 and about 100° C. to form a reaction mixture and, adding to the reaction mixture a cross linking agent and at least one polyol having 2 or more than 2 hydroxyl groups, wherein the cross linking agent is glyoxylic acid, and wherein the adding step is conducted at a pH between about 4.5 and about 6, at a temperature between about 20 and about 100° C. and for a time period of about 0.5 and about 12 hours.
7. The process according to claim 6 , wherein the curing step further comprises heating the resin composition.
8. A substrate made in accordance with the process of claim 6 .
9. The substrate according to claim 8 , wherein the substrate is selected from the group consisting of cellulosic, fiberglass, polymeric materials and composite blends thereof.
10. The substrate according to claim 2 , wherein the substrate is selected from the group consisting of polyester, nylon and cellulosic substrates.