Rigid polyurethane foams with increased heat performance
The present invention provides a rigid polyurethane foam made from the reaction product, at an isocyanate index of from about 90 to about 400, of a polyisocyanate, and a polyol component containing about 20 to about 80 wt. %, based on the weight of the polyol component, of a double metal cyanide (DMC)-catalyzed polyether polyol having a number average molecular weight of greater than about 1000 Daltons (Da), about 80 to about 20 wt. %, based on the weight of the polyol component, of a sucrose-based polyol having a functionality of from about 2.5 to about 6 and a molecular weight of from about 350 to less than about 1,000, and about 0 to about 40 wt. %, based on the weight of the polyol component, of a low molecular weight organic compound having a number average molecular weight of less than about 600 Da, in the presence of water, polyvinylchloride (PVC) particles having a diameter of from about 0.1 to about 200 microns, and glass beads having a diameter of from about 40 to about 400 microns (about 270 to about 45 mesh), and optionally, in the presence of at least one of carbon dioxide, surfactants, flame retardants, pigments and catalysts, wherein the rigid polyurethane foam with a density of about 10 to about 25 pcf has a heat sag measured at 102 mm overhang at 121° C. and one hour of less than about 8 mm. The inventive rigid polyurethane foams exhibit increased heat performance (decreased heat sag) while also maintaining impact and rebound strengths.
1. A rigid polyurethane foam comprising the reaction product, at an isocyanate index of from about 90 to about 400, of:
a polyisocyanate; and
a polyol component comprising
about 20 to about 80 wt. %, based on the weight of the polyol component, of a double metal cyanide (DMC)-catalyzed polyether polyol having a number average molecular weight of greater than about 1000 Daltons (Da),
about 80 to about 20 wt. %, based on the weight of the polyol component, of a sucrose-based polyol having a functionality of from about 2.5 to about 6 and a number average molecular weight of from about 350 to less than about 1,000 Da, and
about 0 to about 40 wt. %, based on the weight of the polyol component, of a low molecular weight organic compound having a number average molecular weight of less than about 600 Da;
in the presence of
water,
polyvinylchloride (PVC) particles having a diameter of from about 0.1 to about 200 microns, and
glass beads having a diameter of from about 40 to about 400 microns (about 270 to about 45 mesh), and
optionally, in the presence of at least one of carbon dioxide, surfactants, flame retardants, pigments and catalysts,
wherein the rigid polyurethane foam with a density of about 10 to about 25 pcf has a heat sag measured at 102 mm overhang at 121° C. and one hour of less than about 8 mm.
2. The rigid polyurethane foam according to claim 1 , wherein the polyisocyanate is selected from the group consisting of ethylene diisocyanate, 1,4-tetramethylene diisocyanate, 1,6-hexamethylene diisocyanate, 1,12-dodecane diisocyanate, cyclobutane-1,3-diisocyanate, cyclohexane-1,3-and -1,4-diisocyanate, 1-isocyanato-3,3,5-trimethyl-5-isocyanatomethyl-cyclohexane (isophorone diisocyanate), 2,4- and 2,6-hexahydrotoluene diisocyanate, dicyclohexylmethane-4,4′-diisocyanate (hydrogenated MDI, or HMDI), 1,3- and 1,4-phenylene diisocyanate, 2,4- and 2,6-toluene diisocyanate (TDI), diphenylmethane-2,4′- and/or -4,4′-diisocyanate (MDI), naphthylene-1,5-diisocyanate, triphenyl-methane-4,4′,4″-triisocyanate, polyphenyl-polymethylene-polyisocyanates (crude MDI or PMDI), norbornane diisocyanates, m- and p-isocyanatophenyl sulfonylisocyanates, perchlorinated aryl polyisocyanates, carbodiimide-modified polyisocyanates, urethane-modified polyisocyanates, allophanate-modified polyisocyanates, isocyanurate-modified polyisocyanates, urea-modified polyisocyanates, biuret containing polyisocyanates and isocyanate-terminated prepolymers.
3. The rigid polyurethane foam according to claim 1 , wherein the polyisocyanate is modified crude MDI or PMDI.
4. The rigid polyurethane foam according to claim 1 , wherein the polyvinylchloride (PVC) particles have a diameter of from about 0.1 to about 50 microns.
5. The rigid polyurethane foam according to claim 1 , wherein the glass beads have a diameter of from about 25 to about 150 microns.
6. The rigid polyurethane foam according to claim 1 , wherein the double metal cyanide (DMC)-catalyzed polyether polyol comprises from about 30 to about 70 wt. %, based on the weight of the polyol component.
7. The rigid polyurethane foam according to claim 1 , wherein the sucrose-based polyol comprises from about 30 to about 70 wt. %, based on the weight of the polyol component.
8. The rigid polyurethane foam according to claim 1 , wherein the sucrose-based polyol has a number average molecular weight of from about 600 to less than about 1,000 Da.
9. The rigid polyurethane foam according to claim 1 , wherein the low molecular weight organic compound comprises from about 0 to about 20 wt. %, based on the weight of the polyol component.
10. The rigid polyurethane foam according to claim 1 , wherein the isocyanate index is from about 95 to about 150.
11. The rigid polyurethane foam according to claim 1 , wherein the rigid polyurethane foam has a heat sag measured at 102 mm overhang at 121° C. and one hour of less than about 5 mm.
12. The rigid polyurethane foam according to claim 1 , wherein the rigid polyurethane foam has a heat sag measured at 102 mm overhang at 121° C. and one hour of less than about 3 mm.
13. A process for making a rigid polyurethane foam comprising reacting at an isocyanate index of from about 90 to about 400:
a polyisocyanate; with
a polyol component comprising
about 20 to about 80 wt. %, based on the weight of the polyol component, of a double metal cyanide (DMC)-catalyzed polyether polyol having a number average molecular weight of greater than about 1000 Daltons (Da),
about 80 to about 20 wt. %, based on the weight of the polyol component, of a sucrose-based polyol having a functionality of from about 2.5 to about 6 and a molecular weight of from about 350 to less than about 1,000 Da, and
about 0 to about 40 wt. %, based on the weight of the polyol component, of a low molecular weight organic compound having a number average molecular weight of less than about 600 Da;
in the presence of
water,
polyvinylchloride (PVC) particles having a diameter of from about 0.1 to about 200 microns, and
glass beads having a diameter of from about 40 to about 400 microns (about 270 to about 45 mesh), and
optionally, in the presence of at least one of carbon dioxide, surfactants, flame retardants, pigments and catalysts,
wherein the rigid polyurethane foam with a density of about 10 to about 25 pcf has a heat sag measured at 102 mm overhang at 121° C. and one hour of less than about 8 mm.
14. The process according to claim 13 , wherein the at least one polyisocyanate is selected from the group consisting of ethylene diisocyanate, 1,4-tetramethylene diisocyanate, 1,6-hexamethylene diisocyanate, 1,12-dodecane diisocyanate, cyclobutane-1,3-diisocyanate, cyclohexane-1,3-and -1,4-diisocyanate, 1-isocyanato-3,3,5-trimethyl-5-isocyanatomethyl-cyclohexane (isophorone diisocyanate), 2,4- and 2,6-hexahydrotoluene diisocyanate, dicyclohexylmethane-4,4′-diisocyanate (hydrogenated MDI, or HMDI), 1,3- and 1,4-phenylene diisocyanate, 2,4- and 2,6-toluene diisocyanate (TDI), diphenylmethane-2,4′- and/or -4,4′-diisocyanate (MDI), naphthylene-1,5-diisocyanate, triphenyl-methane-4,4′,4″-triisocyanate, polyphenyl-polymethylene-polyisocyanates (crude MDI), norbornane diisocyanates, m- and p-isocyanatophenyl sulfonylisocyanates, perchlorinated aryl polyisocyanates, carbodiimide-modified polyisocyanates, urethane-modified polyisocyanates, allophanate-modified polyisocyanates, isocyanurate-modified polyisocyanates, urea-modified polyisocyanates, biuret containing polyisocyanates and isocyanate-terminated prepolymers.
15. The process according to claim 13 , wherein the polyisocyanate is modified crude MDI or PMDI.
16. The process according to claim 13 , wherein the polyvinylchloride (PVC) particles have a diameter of from about 0.1 to about 50 microns.
17. The process according to claim 13 , wherein the glass beads have a diameter of from about 25 to about 150 microns.
18. The process according to claim 13 , wherein the double metal cyanide (DMC)-catalyzed polyether polyol comprises from about 30 to about 70 wt. %, based on the weight of the polyol component.
19. The process according to claim 13 , wherein the sucrose-based polyol comprises from about 30 to about 70 wt. %, based on the weight of the polyol component.
20. The process according to claim 13 , wherein the sucrose-based polyol has a number average molecular weight of from about 600 to less than about 1,000 Da.
21. The process according to claim 13 , wherein the low molecular weight organic compound comprises from about 0 to about 20 wt. %, based on the weight of the polyol component.
22. The process according to claim 13 , wherein the isocyanate index is from about 95 to about 150.
23. The process according to claim 13 , wherein the rigid polyurethane foam has a heat sag measured at 102 mm overhang at 121° C. and one hour of less than about 5 mm.
24. The process according to claim 13 , wherein the rigid polyurethane foam has a heat sag measured at 102 mm overhang at 121° C. and one hour of less than about 3 mm.