FCC catalyst, its preparation and use
A process for preparing a catalyst is disclosed. The process generally comprises the steps of: (a) preparing a slurry comprising clay, zeolite, a sodium-free silica source, quasi-crystalline boehmite, and micro-crystalline boehmite, provided that the slurry does not comprise peptized quasi-crystalline boehmite; (b) adding a monovalent acid to the slurry; (c) adjusting the pH of the slurry to a value above about 3, and (d) shaping the slurry to form particles. This process results in attrition resistant catalysts with a good accessibility.
1. A process for the preparation of a catalyst comprising the steps of:
a) preparing a slurry comprising clay, zeolite, a sodium-free silica source, quasi-crystalline boehmite, and micro-crystalline boehmite, provided that the slurry does not comprise peptised quasi-crystalline boehmite,
b) adding a monovalent acid to the slurry,
c) adjusting the pH of the slurry to a value above 3, and
d) shaping the slurry to form particles;
wherein the slurry contains 1 to 50 wt % of quasi-crystalline boehmite, and 1 to 50 wt % of micro-crystalline boehmite, wherein the weight percentages are based on dry solids content and calculated as oxides.
2. The process according to claim 1 wherein the sodium-free silica source is selected from the group consisting are sodium-free silica sol, polysilicic acid, potassium silicate, lithium silicate, calcium silicate, magnesium silicate, barium silicate, strontium silicate, zinc silicate, phosphorus silicate, and borium silicate, polyorganosiloxanes, methyl chlorosilane, dimethyl chlorosilane, trimethyl chlorosilane, and mixtures thereof.
3. The process according to claim 1 wherein the pH in step c) is adjusted to a value of between 4 and 7.
4. A catalyst composition comprising clay, zeolite, a sodium-free silica source, quasi and micro-crystalline boehmite, wherein the composition is prepared by a) preparing a slurry comprising clay, zeolite, a sodium-free silica source, quasi-crystalline boehmite, and micro-crystalline boehmite, provided that the slurry does not comprise peptised quasi-crystalline boehmite; b) adding a monovalent acid to the slurry; c) adjusting the pH of the slurry to a value above about 3, and d) shaping the slurry to form particles; wherein the slurry contains 1 to 50 wt % of quasi-crystalline boehmite, and 1 to 50 wt % of micro-crystalline boehmite, wherein the weight percentages are based on dry solids content and calculated as oxides.
5. A catalyst composition comprising micro-crystalline boehmite, quasi-crystalline boehmite, zeolite, and silica, wherein the composition contains 1 to 50 wt % of quasi-crystalline boehmite, and 1 to 25 wt % of micro-crystalline boehmite, wherein the weight percentages are calculated as oxides.
6. The process according to claim 1 wherein the zeolite is selected from the group consisting of Y-zeolite, ZSM-5, phosphorus-activated ZSM-5, ion-exchanged ZSM-5, MCM-22, and MCM-36, metal-exchanged zeolites, ITQs, SAPOs, ALPOs, and mixtures thereof.
7. The process according to claim 1 wherein the zeolite has a sodium content of less than 1.5 wt % Na 2 O.