There is provided a method for producing a silver powder having excellent dispersibility and capable of forming a paste which do not form suspended matters by phase separation and which is printed on a substrate to form a film having a uniform thickness. In this method, an alkali or a complexing agent is added to an aqueous silver salt containing solution to form a silver oxide containing slurry or an aqueous silver complex salt containing solution. After or before silver particles are deposited by reduction by adding a reducing agent to the silver oxide containing slurry or aqueous silver complex salt containing solution while stirring it, at least one chelating agent selected from the group consisting of compounds having an azole structure, dicarboxylic acids, hydroxy carboxylic acids and salts thereof is added to a silver power containing slurry solution as a dispersing agent.
1. A silver powder having a tap density of 2 g/cm 3 or more, a mean particle diameter of 0.1 to 5 μm which is measured by a laser diffraction method, a specific surface area of 5 m 2 /g or less, and an angle of repose of 50° or less.
2. A silver powder as set forth in claim 1 , wherein said angle of repose is 45° or less.
3. A silver powder as set forth in claim 1 , wherein a film formed by printing a paste, which is prepared by using said silver powder, on a substrate has a surface roughness of 3 μm or less, and wherein silver particles in said paste has a maximum particle diameter of 30 μm or less which is measured by a grind gauge.
4. A silver powder as set forth in claim 3 , wherein said maximum particle diameter of said silver particles in said paste is 15 μm or less.
5. A silver powder as set forth in claim 3 , wherein said maximum particle diameter of said silver particles in said paste is 7.5 μm or less.