Optically active glass and optical fiber with reduced photodarkening and method for reducing photodarkening
An optically active glass and an optical fiber comprising such glass, having reduced photodarkening properties are provided. The optically active glass is mainly composed of silica representing from about 50 to 98 mol % of the glass. It also includes at least one active ion, such as a rear-earth ion, which induces a photodarkening effect in optical properties of the glass. Moreover, the glass includes an effective amount of phosphorus oxide providing the photodarkening reducing effect, preferably in an amount of from about 1 to 30 mol %. A method for reducing a photodarkening effect in optical properties of an optically active glass including the step of introducing phosphorus oxide to the glass is also provided.
1. An optically active glass comprising:
from about 50 to 98 mol % of silica;
from 0.01 to about 5 mol % of at least one active ion other than erbium for generating or amplifying light, said active ion inducing a photodarkening effect in optical properties of said optically active glass; and
an effective amount of phosphorus oxide for reducing said photodarkening effect.
2. The optically active glass according to claim 1 , wherein said at least one active ion is a rare-earth ion.
3. The optically active glass according to claim 2 , wherein said rare-earth ion is ytterbium or thulium.
4. The optically active glass according to claim 1 , wherein said phosphorus oxide is present in an amount of from about 1 to 30 mol %.
5. The optically active glass according to claim 1 , further comprising from 0.01 to about 30 mol % of at least one co-dopant.
6. The optically active glass according to claim 5 , wherein the co-dopant is an oxide of Al, an oxide of La, an oxide of Lu, an oxide of P, an oxide of Ge, an oxide of Ti, an oxide of F, an oxide of B or a mixture thereof.
7. The optically active glass according to claim 6 , wherein the co-dopant is Al 2 O 3 .
8. The optically active glass according to claim 7 , wherein Al 2 O 3 is present in an amount of about 1 mol %.
9. The optically active glass according to claim 1 , wherein said phosphorus oxide substantially eliminates said photodarkening effect.
10. An optical fiber comprising an optically active glass as defined in claim 1 .
11. The optical fiber according to claim 10 , wherein the optically active glass is comprised in a core and said core is surrounded by at least one cladding.
12. The optical fiber according to claim 11 , wherein each of said at least one cladding consists essentially of pure silica or silica doped with at least one rare-earth element.
13. The optical fiber according to claim 11 , wherein the optically active glass further comprises from 0.01 to about 30 mol % of at least one co-dopant.
14. The optical fiber according to claim 13 , wherein the co-dopant is an oxide of Al, an oxide of La, an oxide of Lu, an oxide of P, an oxide of Ge, an oxide of Ti, an oxide of F, an oxide of B or a mixture thereof.
15. The optical fiber according to claim 14 , wherein the co-dopant is Al 2 O 3 .
16. The optical fiber according to claim 15 , wherein Al 2 O 3 is present in an amount of about 1 mol %.
17. The optical fiber according to claim 10 , wherein said phosphorus oxide substantially eliminates said photodarkening effect.
18. An optically active glass comprising:
about 90 mol % of silica;
about 1 mol % of Yb 2 O 3 ;
about 1 mol % of Al 2 O 3 ; and
about 8 mol % of phosphorus oxide.
19. An optical fiber comprising an optically active glass as defined in claim 18 .
20. The optical fiber according to claim 19 , wherein the optically active glass is comprised in a core and said core is surrounded by at least one cladding.
21. A method for reducing a photodarkening effect in optical properties of an optically active silica glass comprising at least one active ion other than erbium for generating or amplifying light, said at least one active ion inducing said photodarkening effect, the method comprising a step of doping the silica glass with an effective amount of phosphorus oxide.
22. The method of claim 21 , wherein said at least one active ion is ytterbium or thulium.
23. The method of claim 21 , wherein said optically active silica glass comprises from 0.01 to about 5 mol % of Yb 2 O 3 and the effective amount of phosphorus oxide is of from about 1 to 30 mol %.