Fiber optic sensor and method for making
A fiber optic sensor including a fiber having a modified surface integral with the fiber wherein the modified surface includes an open pore network with optical agents dispersed within the open pores of the open pore network. Methods for preparing the fiber optic sensor are also provided. The fiber optic sensors can withstand high temperatures and harsh environments.
1. A fiber optic sensor comprising a fiber having a cladding and a modified surface integral with the fiber said modified surface prepared by applying ceramic material to the fiber and comprising an open pore network and optical agents dispersed within the open pores of the open pore network wherein the modified surface is intimately bonded to the fiber surface, said optical agents comprise a Group 8-10 transition metal or a metal oxide selected from the group consisting of tin dioxide, yttrium oxide, vanadium oxide, titanium oxide and tungsten oxide and said modified surface is on the cladding.
2. The sensor of claim 1 wherein the ceramic material comprises a silica.
3. The sensor of claim 1 wherein the optical agents are transition metals selected from the group consisting of ruthenium, rhodium, platinum and palladium.
4. The sensor of claim 3 wherein the transition metal is palladium.
5. A process for making a fiber optic sensor comprising applying ceramic material to a fiber having a cladding and forming an open pore network structure, dispersing optical agents within the pores of the open pore network and integrating the ceramic material with the fiber, wherein said step of applying ceramic material consists of applying ceramic material to the cladding and said optical agents comprise a Group 8-10 transition metal or a metal oxide selected from the group consisting of tin dioxide, yttrium oxide, vanadium oxide, titanium oxide and tungsten oxide.
6. The process of claim 5 wherein the ceramic material is applied by coating the fiber cladding.
7. The process of claim 5 wherein the ceramic material is applied to the surface of the fiber cladding by forming a film.
8. The process of claim 5 wherein the fiber cladding surface is modified by coating the surface with a ceramic material.
9. The process of claim 5 wherein the fiber cladding surface is modified by dipping the surface into a solution comprising a ceramic material.
10. The process of claim 5 wherein said ceramic material comprises spherical particles.
11. The process of claim 5 wherein the ceramic material comprises a silica.
12. The process of claim 10 wherein the ceramic material is heat treated to form an open pore network and the modified fiber is dipped into a solution comprising optical agents, whereby the optical agents are dispersed within the pores of the open pore network.
13. The process of claim 5 wherein the optical agent is a transition metal or a metal oxide.
14. The process of claim 13 wherein the transition metal is palladium.
15. The process of claim 5 wherein the fiber is heat treated between about 300° C. and 600° C. for about 1 to about 4 hours.
16. A process for making a fiber optic sensor comprising applying a ceramic material mixture comprising ceramic material and optical agents to a fiber having a cladding, forming an open pore network structure within the ceramic material and integrating the ceramic material with the fiber, wherein said step of applying the ceramic material mixture consists of applying the ceramic material mixture to the cladding and said optical agents comprise a Group 8-10 transition metal or a metal oxide selected from the group consisting of tin dioxide, yttrium oxide, vanadium oxide, titanium oxide and tungsten oxide.
17. The process of claim 16 wherein the ceramic material mixture is applied by coating the fiber cladding.
18. The process of claim 16 wherein the ceramic material mixture is applied to the surface of the fiber cladding by forming a film.
19. The process of claim 16 wherein the fiber cladding surface is modified by dipping the surface into a solution comprising a ceramic material mixture.
20. The process of claim 16 wherein said ceramic material comprises spherical particles.
21. The process of claim 16 wherein the ceramic material comprises a silica.
22. The process of claim 16 wherein the optical agent is a transition metal or a metal oxide.
23. The process of claim 22 wherein the transition metal is palladium.
24. The process of claim 16 wherein the fiber is heat treated between about 300° C. and 600° C. for about 1 to about 4 hours.
25. The process of claim 16 wherein the ceramic material mixture further comprises a polymer.
26. The process of claim 25 wherein the polymer is an organic polymer.
27. A sensor prepared by the process of claim 14 .
28. A sensor prepared by the process of claim 23 .