Recycling

1. A process for recycling a coloured moulded article comprising selecting a coloured blow-moulded article, wherein a thermoplastic blow-moulded material which defines the blow-moulded article is coloured by having a colourant chemically bound to the thermoplastic material of the blow-moulded article on the surface thereof, but substantially none of the colourant being present within the core of the thermoplastic blow-moulded material of the blow-moulded article substantially beneath the coloured surface; contacting the optionally comminuted coloured blow-moulded article with a caustic wash comprising at least 20% w/w alkali metal hydroxide and recovering colour-modified thermoplastic composition from the caustic wash which is substantially devoid of any colourant.

2. A process according to claim 1 , wherein said colourant penetrates at least 0.01% of the thickness of the thermoplastic material.

3. A process according to claim 1 , wherein said colourant penetrates at least 3 μm below the surface.

4. A process according to claim 1 , wherein the ratio of the weight of dry thermoplastic material recovered after said caustic wash to the weight of said coloured thermoplastic material treated in the process is at least 0.6.

5. A process according to claim 1 , wherein the coloured thermoplastic material has a thickness of less than 1 mm.

6. A process according to claim 1 , wherein said coloured thermoplastic material comprises a disperse dye.

7. A process according to claim 1 , wherein said thermoplastic material comprises a polyester.

8. A process according to claim 1 , wherein said thermoplastic material comprises polyethylene terephthalate.

9. A process according to claim 5 , wherein said coloured thermoplastic material is derived from a recyclable moulded article to which colour was imparted prior to an expansion step whereby the recyclable moulded article was formed.

10. A process according to claim 1 , wherein said recyclable moulded article is derived from a coloured precursor moulded article by expansion of said precursor moulded article.

11. A process according to claim 1 , wherein said recyclable moulded article is derived from a coloured precursor moulded article which was blow moulded to define said recyclable moulded article.

12. A process according claim 1 , wherein said coloured thermoplastic material is derived from a polyethylene terephthalate beverage container incorporating a disperse dye.

13. A process according to claim 1 , wherein the caustic wash comprises caustic soda.

14. A process according to claim 9 , wherein the caustic wash is conducted at at least 20° C.

15. A process according to claim 1 , wherein the caustic wash is followed by a drying stage wherein the drying stage comprises drying the washed thermoplastic material under substantially dry air conditions at a temperature of at least about 50° C. over a period of at least about 2 hours.

16. The process of claim 1 , wherein the caustic wash comprises at least about 40% w/w of the alkali metal hydroxide.