Particulate water absorbing agent comprising crosslinked absorbent resin and having low residual monomer, water absorbing article and method for production of water absorbing agent
An object of the present invention is to provide a water absorbing agent having a low amount of residual monomer, small variance of the amount of residual monomer among ranges of particle size distribution and favorable absorption properties, and being sanitary; an absorbing article; and a method for the production of a water absorbing agent. The water absorbing agent of the present invention has the amount of residual monomer of not higher than 500 ppm, and a residual monomer index of not greater than 0.30. The method for the production includes a first step of obtaining a hydrogel polymer by polymerizing an aqueous solution of a monomer including an unsaturated carboxylic acid and/or a salt thereof in the presence of a crosslinking agent; a second step of obtaining a water absorbent resin precursor which is in powder form and includes particles having a particle size of 300 to 850 μm and particles having a particle size of smaller than 300 μm as main components by drying said hydrogel polymer followed by pulverization and classification to adjust the particle size distribution, a third step of obtaining a water absorbent resin by heating a mixture of said water absorbent resin precursor and a surface crosslinking agent, which can form an ester bond around the surface of said water absorbent resin precursor, a fourth step of adding by spraying an aqueous solution that includes a sulfur-containing reducing agent to said water absorbent resin, and a fifth step of subjecting the mixture of the water absorbent resin and said aqueous solution to a heat treatment under an airflow of not lower than 40° C. but not higher than 120° C.
1. A particulate water absorbing agent comprising a water absorbent resin as a principal component,
wherein the absorbent resin has a cross-linked structure including a constitutional unit derived from an unsaturated carboxylic acid and/or a salt thereof and is obtained by a surface crosslinking treatment around the surface thereof with a surface crosslinking agent,
said water absorbing agent comprising particles having a particle size of 300 to 850 μm and particles having a particle size of smaller than 300 μm,
wherein the amount of residual monomer is not lower than 0 but not higher than 500 ppm, and
residual monomer index (RMI) calculated by the following formula (1):
RMI=| RM 1 −RM 2 |/RM A (1)
wherein, RM 1 represents the amount of residual monomer of the water absorbing agent having a particle size of smaller than 300 μm among the particles constituting the water absorbing agent; RM 2 represents the amount of residual monomer of the water absorbing agent having a particle size of 300 to 850 μm among the particles constituting the water absorbing agent; and RM A represents the amount of residual monomer of the water absorbing agent,
is not greater than 0.30.
2. The water absorbing agent according to claim 1 wherein the amount of residual monomer is not lower than 0 but not higher than 300 ppm.
3. The water absorbing agent according to claim 1 wherein main component of said unsaturated carboxylic acid is acrylic acid, and said residual monomer is acrylic acid and/or a salt thereof.
4. The water absorbing agent according to claim 1 wherein weight ratio of particles having a particle size of 300 to 850 μm to particles having a particle size of smaller than 300 μm is not less than 20/80 but not greater than 80/20.
5. The water absorbing agent according to claim 1 wherein absorption capacity without load (CRC) for a physiological saline solution is not less than 30 g/g, and absorption capacity under a high load of 4.8 kPa (AAP 4.8 kPa) for a physiological saline solution is not less than 20 g/g.
6. The water absorbing agent according to claim 1 wherein total absorption capacity (TAC) for a physiological saline solution which is calculated by the following formula (2):
TAC (g/g)=CRC+ SAAP (2)
wherein, CRC represents absorption capacity without load (g/g), and SAAP (Single-layer AAP) represents single-layer absorption capacity under a load of 1.9 kPa (g/g),
is not less than 65 g/g.
7. The water absorbing agent according to claim 1 wherein content of the particles having a particle size of smaller than 150 μm is not higher than 2% by weight.
8. The water absorbing agent according to claim 1 wherein the particle has an irregular pulverized shape.
9. The water absorbing agent according to claim 1 which comprises an oxidizing agent, a reducing agent or a persulfate salt, and a water absorbent resin.
10. The water absorbing agent according to claim 1 which comprises a sulfur-containing reducing agent and a water absorbent resin.
11. A water absorbing agent according to claim 1 wherein the water absorbent resin which has a cross-linked structure including a constitutional unit derived from an unsaturated carboxylic acid and/or a salt thereof and which is obtained by said surface crosslinking treatment around the surface thereof with said surface crosslinking agent; and a sulfur-containing reducing agent,
wherein absorption capacity without load (CRC) for a physiological saline solution is not less than 32 g/g,
absorption capacity under a high load of 4.8 kPa (AAP 4.8 kPa) for a physiological saline solution is not less than 20 g/g,
content of sulfur based volatile component as an atmospheric concentration specified by a gas detector tube is not less than 0 but not higher than 2.5 ppm.
12. An absorbing article which comprises the water absorbing agent according to claim 11 .
13. An absorbing article comprising the water absorbing agent of claim 1 .