Method for steel strip coating and a steel strip provided with said coating
Coating steel strips comprising, in % by weight, C: ≦1.6%, Mn: 6-30%, Al: ≦10%, Ni: ≦10%, Cr: ≦10%, Si: ≦8%, Cu: ≦3%, Nb: ≦0.6%, Ti: ≦0.3%, V: ≦0.3%, P: ≦0.1%, B: ≦0.01%, the rest being iron and unavoidable impurities, and a method of forming steel strips are described. Up to now, such steel strips were not adequately coatable, with a metal coating ensuring outstanding corrosion-resistance and good welding properties. This is ensured by applying an aluminium layer to the steel strip before final annealing and applying the metal coating to said aluminium layer after final annealing.
1. A method for coating a steel strip comprising in % by weight C: ≦1.6%, Mn: 6-30%, Al: ≦10%, Ni: ≦10%, Cr: ≦10%, Si: ≦8%, Cu: ≦3%, Nb: ≦0.6%, Ti: ≦0.3%, V: ≦0.3%, P: ≦0.1%, B: ≦0.01%, N: ≦1.0%, the rest being iron and unavoidable impurities, wherein the steel strip is subjected to final annealing and then coated with a coating of a molten metal, the method comprising:
applying an aluminum layer to the steel strip before final annealing; and
applying the coating of molten metal after final annealing.
2. The method of claim 1 wherein the thickness of the aluminum layer is 50 nm to 1,000 nm.
3. The method of claim 1 wherein the annealing temperature during final annealing performed after application of the aluminum layer is from 680° C. to 900° C.
4. The method of claim 1 wherein the annealing time during final annealing is 30 seconds to 250 seconds.
5. The method of claim 1 wherein the coating of the molten metal is applied by hot dip coating.
6. The method of claim 1 wherein the coating of the molten metal, applied after final annealing, includes at least one of an Al/Si alloy, Al, Zn, Al and Zn, and a zinc alloy.
7. The method of claim 1 wherein a surface of the steel strip is cleaned prior to application of the coating.
8. The method of claim 1 wherein the aluminum layer is applied by PVD coating.
9. The method of claim 2 wherein the annealing temperature during final annealing performed after application of the aluminum layer is from 680° C. to 900° C.
10. The method of claim 2 wherein the annealing time during final annealing is 30 seconds to 250 seconds.
11. The method of claim 10 wherein the annealing time during final annealing is 30 seconds to 250 seconds.
12. A steel strip comprising:
a steel base material, comprising in % by weight C: ≦1.6%, Mn: 6-30%, Al: ≦10%, Ni: ≦10%, Cr: ≦10%, Si: ≦8%, Cu: ≦3%, Nb: ≦0.6%, Ti: ≦0.3%, V: ≦0.3%, P: ≦0.1%, B: ≦0.01%, N: ≦1.0%, the rest being iron and unavoidable impurities;
a metallic coating applied; and
an intermediate layer between the steel base material and the metallic coating, the intermediate layer comprising Al and Fe.
13. The steel strip of claim 12 wherein the thickness of the intermediate layer is 50 nm to 1,000 nm.
14. The steel strip of claim 12 wherein the metallic coating is formed by at least one of an Al/Si alloy, Al, Zn and a Zn-alloy.
15. The steel strip of claim 12 wherein the steel base material has the following composition in % by weight:
C: ≦1.00%,
Mn: 20.0-30.0%,
Al: ≦0.5%,
Si: ≦0.5%,
B: ≦0.01%,
Ni: ≦3.0%,
Cr: ≦10.0%,
Cu: ≦3.0%,
N: <0.6%,
Nb: <0.3%,
Ti: <0.3%,
V: <0.3%,
P: <0.1%,
the rest being iron and unavoidable impurities.
16. The steel strip of claim 12 wherein the steel base material has the following composition in % by weight:
C: ≦1.00%,
Mn: 7.00-30.00%,
Al: 1.00-10.00%,
Si: >2.50-8.00%,
with Al +Si contents >3.50-12.00%,
B: <0.01%,
Ni: <8.00%,
Cu: <3.00%,
N: <0.60%,
Nb: <0.30%,
Ti: <0.30%,
V: <0.30%,
P: <0.01%,
the rest being iron and unavoidable impurities.
17. The steel strip of claim 13 wherein the steel base material has the following composition in % by weight:
C: ≦1.00%,
Mn: 20.0-30.0%,
Al: ≦0.5%,
Si: ≦0.5%,
B: ≦0.01%,
Ni: ≦3.0%,
Cr: ≦10.0%,
Cu: ≦3.0%,
N: <0.6%,
Nb: <0.3%,
Ti: <0.3%,
V: <0.3%,
P: <0.1%,
the rest being iron and unavoidable impurities.
18. The steel strip of claim 13 wherein the steel base material has the following composition in % by weight:
C: ≦1.00%,
Mn: 7.00-30.00%,
Al: 1.00-10.00%,
Si: >2.50-8.00%,
with Al +Si contents >3.50-12.00%,
B: <0.01%,
Ni: <8.00%,
Cu: <3.00%,
N: <0.60%,
Nb: <0.30%,
Ti: <0.30%,
V: <0.30%,
P: <0.01%,
the rest being iron and unavoidable impurities.