Object comprising a friction-reducing coating, and method for the production of a coating
An object has bearing location where the object comes into contact with a counter-piece. The bearing location includes a coating to reduce wear and friction. The coating comprises about 90-100 weight percent thermoplastic polymer and about 0-10 weight percent finely divided solid fillers and finely divided dry lubricants. The coating has a thickness of between about 5-50 μm.
1. An object with a bearing location where the object comes into contact with a counter-piece, the bearing location having a coating, the coating comprising:
about 90-100 weight percent thermoplastic polymer selected from the family of the polyaryletherketones; and
about 0-10 weight percent finely divided solid fillers and finely divided dry lubricants; wherein the coating has a thickness of between about 5-50 μm and the coating forms an outermost surface of the object at the bearing location where the object comes into contact with the counter-piece;
wherein the thickness of the coating is between about 5-30 μm.
2. The object of claim 1 , wherein the coating is free from fluorine-containing polymers.
3. The object of claim 1 , wherein the coating comprises at most about 5% by weight of the finely divided solid fillers.
4. The object of claim 1 , wherein the solid fillers are selected from the group consisting of nano ceramic particles, metallic particles, silica, quartz and diamond.
5. The object of claim 4 , wherein the metallic particles are selected from the group consisting of aluminum, bronze, copper, tin, chromium, nickel, antimony, titanium, zirconium, manganese, cobalt, zinc and the oxides thereof, and iron oxide.
6. The object of claim 1 , wherein the dry lubricant comprises at most 2 percent by weight graphite or molybdenum sulfide.
7. The object of claim 1 , wherein the coating comprises a multilayer structure.
8. The object of claim 7 , wherein the polyaryletherketones comprise PEK, PEKKEK, PEEK, LCP, PPS, or mixtures of PEK and PEEK.
9. The object of claim 1 , wherein a maximum particle size of the fillers is at least an order of magnitude less than the thickness of the coating.
10. The object of claim 1 , wherein the polyaryletherketones comprise one or more of PEEK, PEK, LCP, PPS, or mixtures of PEEK and PEK.
11. The object of claim 1 , wherein the coating further comprises an adhesion promoting layer, the adhesion promotion layer comprising at most about 90 percent by weight of finely divided metallic particles in addition to a thermoplastic polymer.
12. The object of claim 1 , wherein the thickness of the coating is between about 10 μm and 20 μm.
13. An object with a bearing location where the object comes into contact with a counter-piece, the bearing location having a coating, the coating comprising:
about 90-100 weight percent thermoplastic polymer selected from the family of the polyaryletherketones; and
about 0-10 weight percent finely divided solid fillers and finely divided dry lubricants; wherein the coating has a thickness of between about 5-50 μm and the coating forms an outermost surface of the object at the bearing location where the object comes into contact with the counter-piece;
wherein the coating comprises at least 95% by weight of the thermoplastic polymer.
14. The object of claim 13 , wherein the coating is free from fluorine-containing polymers.
15. The object of claim 13 , wherein the coating comprises at most about 5% by weight of the finely divided solid fillers.
16. The object of claim 13 , wherein the solid fillers are selected from the group consisting of nano ceramic particles, metallic particles, silica, quartz and diamond.
17. The object of claim 16 , wherein the metallic particles are selected from the group consisting of aluminum, bronze, copper, tin, chromium, nickel, antimony, titanium, zirconium, manganese, cobalt, zinc and the oxides thereof, and iron oxide.
18. The object of claim 13 , wherein the dry lubricant comprises at most 2 percent by weight graphite or molybdenum sulfide.
19. The object of claim 13 , wherein the coating comprises a multilayer structure.
20. The object of claim 19 , wherein the polyaryletherketones comprise PEK, PEKKEK, PEEK, LCP, PPS, or mixtures of PEK and PEEK.
21. The object of claim 13 , wherein a maximum particle size of the fillers is at least an order of magnitude less than the thickness of the coating.
22. The object of claim 13 , wherein the polyaryletherketones comprise one or more of PEEK, PEK, LCP, PPS, or mixtures of PEEK and PEK.
23. The object of claim 13 , wherein the coating further comprises an adhesion promoting layer, the adhesion promotion layer comprising at most about 90 percent by weight of finely divided metallic particles in addition to a thermoplastic polymer.
24. A method for the application of a coating to an object using a dispersion, the dispersion comprising:
coating components in finely divided dispersed form in a solvent, the components including at least one finely divided thermoplastic polymer is selected from the family of the polyaryletherketones;
applying the dispersion to the object; and
bringing the object to a temperature above a melting point of the thermoplastic polymer to obtain a homogeneous compact coating comprising about 90-100 weight percent thermoplastic polymer selected from a family of the polyaryletherketones and about 0-10 weight percent finely divided solid fillers and finely divided dry lubricants with a layer thickness of between about 5-50 μm, the coating forming an outermost surface of the object at a bearing location where the object comes into contact with a counter-piece;
wherein the object is partially coated.
25. The method of claim 24 , wherein the solvent for dispersion comprises 25-75 percent by weight of isopropanol and water,
wherein the dispersion further comprises polymer, fillers, and about 20-50 percent by weight of finely divided solids.
26. An object with a bearing location where the object comes into contact with a counter-piece, the bearing location having a coating, the coating comprising:
about 90-100 weight percent thermoplastic polymer selected from the family of the polyaryletherketones; and
about 0-10 weight percent finely divided solid fillers and finely divided dry lubricants; wherein the coating has a thickness of between about 5-50 μm and the coating forms an outermost surface of the object at the bearing location where the object comes into contact with the counter-piece;
wherein the object comprises a sliding bearing.