Water-borne primer coating composition and method of forming coating film
View Patent ↗A water-borne primer coating composition including a water-borne non-chlorinated polyolefin resin (A), a water-borne polyurethane resin (B), a water-borne epoxy resin (C) and an internally crosslinked acrylic particle emulsion (D), wherein the content of resin (A) is 15 to 60%, the content of resin (B) is 10 to 50%, the content of resin (C) is 20 to 50%, and the content of emulsion (D) is 5 to 20%, all by weight on the solid equivalent basis in 100% by weight of the total amount of resin (A), resin (B), resin (C) and emulsion (D), and resin (A) is a polypropylene resin having crystallinity of 35 to 55% and a weight average molecular weight of 50000 to 200000. The composition can achieve an adhesion property to a substrate, gasohol resistance, inhibition of peeling of a multilayer coating film in washing by high pressure cleaning and moisture resistance.
1. A water-borne primer coating composition including a water-borne non-chlorinated polyolefin resin (A), a water-borne polyurethane resin (B), a water-borne epoxy resin (C) and an internally crosslinked acrylic particle emulsion (D),
wherein the content of said resin (A) is 15 to 60% by weight,
the content of said resin (B) is 10 to 50% by weight,
the content of said resin (C) is 20 to 50% by weight, and
the content of said emulsion (D) is 5 to 20% by weight
on the solid equivalent basis in 100% by weight of the total amount of said resin (A), resin (B), resin (C) and emulsion (D),
said resin (A) is a water-borne polypropylene resin having crystallinity of 35 to 55% and a weight average molecular weight of 50000 to 200000 and being converted to a water-borne resin without using an emulsifier,
wherein the resin (A) is obtained by using a metallocene catalyst, and
wherein the emulsion (D) is obtained by emulsion polymerization of a monomer composition including an ethylenic unsaturated monomer and a crosslinkable monomer, and
a glass transition temperature of a non-crosslinked polymer obtained by polymerization of said ethylenic unsaturated monomer is 50 to 140° C., and
the content of said crosslinkable monomer is 0.1 to 50% by weight in 100% by weight of said monomer composition.
2. The water-borne primer coating composition according to claim 1 , wherein the water-borne non-chlorinated polypropylene resin includes a homopolymer of propylene and a copolymer of propylene and a monomer which can be copolymerized with propylene and does not contain chlorine.
3. A method of forming a coating film, comprising the steps of applying the water-borne primer coating composition according to claim 1 to a substrate and applying a top coating composition.