Method for making oriented single-walled carbon nanotube/polymer nano-composite membranes
View Patent ↗Nano-composite membranes and methods for making them are described. The nano-composite membranes a made from a layer of oriented carbon nanotubes fixed in a polymeric matrix. Methods for efficient, facile, and inexpensive fabrication of the nano-composite membranes using a filtration method are also described. The carbon nanotubes may also be modified with chemical functional groups to promote their orientation in the carbon nanotube layer or to confer to them other properties.
1. A method of making a composite membrane comprising the steps of:
providing a dispersion of carbon nanotubes, wherein the dispersion comprises the carbon nanotubes at a concentration less than about 10×10 −5 % (wt.) and a surfactant;
orienting the majority of the carbon nanotubes on and in a direction perpendicular to a filter by filtration alone, wherein the pore size of the filter is about 0.22 μm or smaller;
providing a polymer matrix comprising a polymer and a diluting solvent;
casting the polymer matrix onto the layer of oriented carbon nanotubes;
removing diluting solvent from the composite; and
annealing the polymer thereby forming a nano-composite membrane.
2. The method of making a composite membrane according to claim 1 , wherein the carbon nanotubes are dispersed in a dispersing solvent.
3. The method of making a composite membrane according to claim 1 , wherein the polymer matrix is cast using a spin coating method.
4. The method of making a composite membrane according to claim 1 , wherein the polymer matrix is cast by layering the polymer diluted in the diluting solvent on a substrate and causing oriented carbon nanotubes to come in contact with the layer of diluted polymer.
5. The method of making a composite membrane according to claim 1 , wherein the annealing step comprises placing the composite membrane in a vacuum and heating the composite membrane to at least about the glass transition temperature of the polymer being used to form the polymer matrix.
6. The method of making a composite membrane according to claim 1 , wherein the oriented carbon nanotubes comprise oriented multi-walled, double-walled and single-walled carbon nanotubes.
7. The method of making a composite membrane according to claim 1 , wherein the carbon nanotubes have diameters from about 0.8 nm to about 50 nm.
8. The method of making a composite membrane according to claim 1 , wherein the oriented carbon nanotubes comprise carbon nanotubes which have been chemically modified with functional groups.
9. The method of making a composite membrane according to claim 8 , wherein the chemical modifying groups are selected from the group consisting of:
carboxylic acid, amine, alkane, alkene, alkyne, alkoxy, ether, ester, cyano, silyl, sulfonic acid, phosphoric acid and boronic acid functional groups.
10. The method of making a composite membrane according to claim 8 , wherein the chemical modifying group is a zwitterion.
11. The method of making a composite membrane as recited in claim 1 , wherein said polymer matrix comprises a polymer selected from the group consisting of:
a polyimide; a polysulfone; a cellulose acetate; a polycarbonate; a polymethacrylate; other thermoplastic polymers and other glassy polymers.
12. The method of claim 1 , wherein the carbon nanotube is hydrophilic and the filter is hydrophobic.