Method of manufacturing colored lens
A method of manufacturing a colored lens includes: applying a coating liquid for forming a dyeable hard coat layer over a lens substrate; firstly heating the lens substrate coated with the coating liquid after the coating step at a temperature of T 1 ° C. for t 1 hours; dyeing the heated lens substrate by dipping it in a dyeing liquid after the first heating step; and secondly heating the lens substrate which is dyed after the dyeing step at a temperature of T 2 ° C. for t 2 hours, wherein the following expression is satisfied when the product of the temperature T 1 and the time t 1 is a first management value Q 1 and the product of the temperature T 2 and the time t 2 is a second management value Q 2: 0.2< Q 1 /( Q 1+ Q 2 )≦ 0.5.
1. A method, of manufacturing a colored lens, comprising:
applying a coating liquid for forming a dyeable hard coat layer over a lens substrate to provide a coated substrate;
firstly heating the coated substrate at a temperature of T 1 ° C. for t 1 hours to provide a heated lens substrate;
dyeing the heated lens substrate by dipping it in a dyeing liquid after the first heating step to provide a dyed lens; and
heating the dyed lens at a temperature of T 2 ° C. for t 2 hours;
wherein the following expression is satisfied when the product of the temperature T 1 and the time t 1 is a first management value Q 1 and the product of the temperature T 2 and the time t 2 is a second management value Q 2 :
0.2< Q 1/( Q 1+ Q 2)≦0.5;
wherein the sum of the time t 1 and the time t 2 satisfies the following requirement:
1 hour≦( t 1 +t 2 )≦3 hours.
2. The method of manufacturing a colored lens according to claim 1 , wherein the temperature T 1 and the temperature T 2 satisfy the following requirements:
100° C.<T 1 <150° C.; and
100° C.<T 2 <150° C.
3. The method of manufacturing a colored lens according to claim 1 , wherein the dyeable hard coat layer includes fine metal-oxide particles, a silicon compound, and a polyfunctional epoxy compound as main components.
4. A colored lens manufacturing method, comprising:
heating a coated lens in a first heating step; then
dyeing the lens in a dyeing liquid; and then
heating the lens in a second heating step;
wherein the ratio of the heat provided over time in the first heating step, to the total amount of the heat provided over time in the first and second heating steps taken together, is not more than 0.5;
wherein the combined duration of the first and second heating steps is from 1 to 3 hours, inclusive.
5. The colored lens manufacturing method as set forth in claim 4 , wherein the ratio is greater than 0.2.
6. The colored lens manufacturing method as set forth in claim 5 , wherein the temperature in the first and second heating steps is between 100 and 150 degrees Celsius.
7. The colored lens manufacturing method as set forth in claim 6 , wherein a dyeable hard coat layer of the coated lens includes fine metal-oxide particles, a silicon compound, and a polyfunctional epoxy compound as main components.