Nanothin polymer coatings containing thiol and methods of use thereof
View Patent ↗The present invention provides a new monomer and methods of using the monomer to fabricate robust polymer surface coatings with controlled thicknesses between 1 and 5 nanometers. The coatings are composed of a new material containing polymerized monomers of 4-vinylbenzenepropanethiol. The polymer surface coating may be applied to metal and silicon. The method includes exposing a metal substrate to a solution of the monomer in hexanes in order to deposit a monolayer of the monomer onto the metal surface. The substrate is then irradiated with ultraviolet radiation in order to graft a thin polymer coating onto the surface. The procedure can be repeated in order to control the thickness of the coating between about 1 nm and 5 nm. Alternatively, thermally initiated polymerization or deposition of partially oligomerized monomers onto the surface provides nanothin coatings with identical performance. The coating provides complete surface coverage, is extremely robust, and exhibits excellent insulating and anti-corrosive properties.
1. A compound having the formula:
2. A polymer of the compound of claim 1 .
3. The polymer of claim 2 , wherein the polymer has a thickness of from about 1 to about 10 nanometers.
4. A method of applying a compound to a metal, comprising:
providing 4-vinylbenzenepropanethiol as a solution in an organic solvent;
providing a metal;
placing the metal in the solution of 4-vinylbenzenepropanethiol so that the solution is in contact with the metal surface;
exposing the mixture to ultraviolet radiation.
5. The method of claim 4 , wherein exposing the mixture to ultraviolet radiation further comprises exposing the mixture to ultraviolet radiation having a wavelength of from about 200 nanometers to about 300 nanometers for a duration of from about 10 minutes to about 1 hour.
6. The method of claim 5 , wherein exposing the mixture to ultraviolet radiation further comprises exposing the mixture to ultraviolet radiation having a wavelength of about 255 nanometers for a duration of from about 10 minutes to about 1 hour.
7. The method of claim 6 , wherein the metal is selected from a group consisting of copper, gold, platinum, and iron.
8. A method of applying a compound to a metal, comprising:
providing 4-vinylbenzenepropanethiol;
providing a metal in hexane;
placing the 4-vinylbenzenepropanethiol in the hexane with the metal in order to prepare a mixture;
adding a thermal free radical initiator such as benzoyl peroxide to the mixture;
incubating the mixture at from about 50 degrees Celsius to about 90 degrees Celsius.
9. The method of claim 8 , wherein the incubating mixture further comprises incubating for from about 15 minutes to about 24 hours.
10. The method of claim 8 , wherein the thermal free radical initiator is benzoyl peroxide.
11. A method of applying a compound to a metal, comprising:
providing 4-vinylbenzenepropanethiol;
exposing the 4-vinylbenzenepropanethiol to air at room temperature for from about 30 minutes to about 24 hours;
diluting the 4-vinylbenzenepropanethiol and its oligomers in an organic solvent to about 1% w/w;
contacting the metal with the solution of 4-vinylbenzenepropanethiol and its oligomers.
12. The method of claim 11 , further comprising incubating the metal in the solution of 4-vinylbenzenepropanethiol for from about 10 seconds to about 40 hours.
13. The method of claim 12 , wherein incubating the metal in the solution of 4-vinylbenzenepropanethiol is from about 10 seconds to about 30 minutes.
14. A method of making 4-vinylbenzenepropanethiol, comprising:
providing 1-bromo-3-phenylpropane
adding acetic anhydride and aluminum chloride;
incubating the mixture at from about −20 to about 20 degrees Celsius for from about 1 hour to about 12 hours;
isolating the resulting p-(3-bromopropyl)acetophenone;
adding sodium borohydride to the p-(3-bromopropyl)acetophenone solution in methanol;
incubating the mixture at about 0 degrees Celsius for about 2 hours;
isolating the resulting p-(3-bromopropyl)-α-methylbenzenemethanol;
adding toluensulfonic acid to the solution of p-(3-bromopropyl)-α-methylbenzenemethanol in toluene;
refluxing the mixture under inert atmosphere for about 4 hours;
isolating the resulting p-(3-Bromopropyl)styrene;
adding thiourea to the p-(3-Bromopropyl)styrene;
gently refluxing the mixture for about 16 hours;
adding sodium hydroxide;
gently refluxing the mixture for about 4 hours.