Method of producing ceramic structure and ceramic structure
Striped sheets each having a structure in which two types of first layers and second layers are stacked in the X direction are prepared. More specifically, first raw material sheets having the same composition as the first layers and second raw material sheets having the same composition as the second layers are regularly alternately stacked in the X direction to prepare a uniaxial stack. The uniaxial stack is then cut along the X direction to prepare the striped sheets. A large number of striped sheets and a large number of homogeneous sheets are then collected to form a sheet group. The striped sheets and the homogeneous sheets are alternately stacked in the Y direction different from the X direction to prepare a biaxial stack having two stacking axes in the X direction and the Y direction. The biaxial stack is fired to produce a ceramic structure.
1. A ceramic structure comprising:
a sheet group including striped sheets, each striped sheet being formed of two or more types of unfired ceramic layers that are stacked,
wherein the sheet group is stacked in a direction different from the stacking direction of the two or more types of unfired ceramic layers.
2. The ceramic structure according to claim 1 , wherein the sheet group comprises other sheets different from the striped sheets.
3. The ceramic structure according to claim 1 , wherein layers of the same type in each of the striped sheets are arrayed in a checkered pattern along the stacking direction of the sheet group including the striped sheets.
4. A ceramic structure comprising:
grid pattern sheets comprising a plurality of striped blocks and a plurality of homogenous blocks, the striped blocks comprising a stacked structure of two or more types of unfired ceramic layers, the striped blocks being stacked in a direction different from a stacking direction of the unfired ceramic layers,
wherein a sheet group including the grid-patterned sheets is stacked in a direction different from both the stacking direction of the unfired ceramic layers and a stacking direction of the striped blocks.
5. The ceramic structure according to claim 4 , wherein the grid-patterned sheets each comprise the striped blocks and other blocks different from the striped blocks which are stacked with each other.
6. The ceramic structure according to claim 4 , wherein the sheet group comprises other sheets different from the grid-patterned sheets.
7. The ceramic structure according to claim 4 , wherein unfired ceramic layers of the same type in each of the grid-patterned sheets are arrayed in a checkered pattern along the stacking direction of the sheet group including the grid-patterned sheets.