Use of polypeptides in the form of adhesive agents
A multilayered composite or coated substrate, comprising compounds of which at least 40% by weight are composed of alpha-amino acids linked via peptide bonds as adhesion promoters between at least two adjacent layers of the composite or between the coating and the substrate.
1. A coated metallic substrate comprising a compound between the coating and the substrate, wherein at least 40% by weight of the compound consists of a polypeptide as an adhesion promoter between the coating and the substrate, wherein the polypeptide is a hydrophobin of the formula
X n —C 1 —X 5-9 —C 2 —C 3 —X 11-39 —C 4 —X 2-23 —C 5 —X 5-9 —C 6 —C 7 —X 6-18 —C 8 —X m (III),
wherein each amino acid residue of each X independently is a naturally occurring amino acid Phe, Leu, Ser, Tyr, Cys, Trp, Pro, His, Gln, Arg, Ile, Met, Thr, Asn, Lys, Val, Ala, Asp, Glu, Gly; each numerical subscript designates the number of amino acid residues of its adjacent X; subscripts n and m independently designate the number of amino acids from 0 to 500, inclusive, of its adjacent X; and each C independently is Cys, Ala, Ser, Gly, Met or Thr, provided that at least seven of the C residues are Cys, wherein said polypeptide has a property in increasing the contact angle of a water drop on a glass surface coated with said polypeptide by at least 20° as compared to the contact angle of a water drop of similar size on an uncoated glass surface as measured at room temperature, and wherein the substrate comprises steel, steel coated with zinc, zinc alloys, aluminum or aluminum alloys.
2. The coated metallic substrate of claim 1 , wherein in the formula (III) the subscripts n and m independently designate the number of amino acids from 15 to 300, inclusive, of the X adjacent each n and m.
3. The coated metallic substrate of claim 1 , wherein the coating comprises a paint layer.
4. The coated metallic substrate of claim 1 , wherein the substrate-facing surface of the coating consists of a natural or synthetic polymer.
5. The coated metallic substrate of claim 1 , wherein the substrate consists of galvanized steel.
6. The coated metallic substrate of claim 1 , wherein the polypeptide improves adhesion of the coating and the substrate.
7. A process for preparing the coated metallic substrate of claim 1 , comprising:
applying the polypeptide to the substrate as an aqueous solution,
performing a drying procedure, and
applying the coating to the polypeptide-treated substrate.
8. The process of claim 7 , wherein the coating is applied as an aqueous solution or dispersion, and the drying procedure is performed after application of the coating.
9. The process of claim 8 , wherein the aqueous solution or dispersion is an aqueous dispersion of an emulsion polymer.
10. A process for preparing the coated metallic substrate of claim 1 , comprising:
applying the polypeptide to a surface of the substrate or a substrate-facing surface of a coating agent,
performing a drying procedure if the polypeptide is applied as an aqueous solution, and
subsequently applying the coating agent to the substrate.
11. A process for preparing the coated metallic substrate of claim 1 , comprising:
applying the polypeptide to a surface of the substrate,
performing a drying procedure if the polypeptide is applied as an aqueous solution, and
preparing the coating by forming a film of a natural or synthetic polymer on the substrate surface.
12. The process of claim 11 , wherein the natural or synthetic polymer is in form of an aqueous solution or dispersion, and a drying procedure is carried out after formation of the film.
13. The process of claim 12 , wherein the aqueous solution or dispersion is an aqueous dispersion of an emulsion polymer.
14. The process of claim 7 , wherein the coating is a paint.