Methods of use of calcium hexa aluminate refractory linings and/or chemical barriers in high alkali or alkaline environments
A method for improving the insulating character/and or penetration resistance of a liner in contact with at least one of an alkali and/or alkaline environments is provided. The method comprises lining a surface that is subject to wear by an alkali environment and/or an alkaline environment with a refractory composition comprising a refractory aggregate consisting essentially of a calcium hexa aluminate clinker having the formula CA 6 , wherein C is equal to calcium oxide, wherein A is equal to aluminum oxide, and wherein the hexa aluminate clinker has from zero to less than about fifty weight percent C 12 A 7 , and wherein greater than 98 weight percent of the calcium hexa aluminate clinker having a particle size ranging from −20 microns to +3 millimeters, for forming a liner of the surface. This method improves the insulating character/and or penetration resistance of the liner.
1. A method for manufacturing a black liquor gasifier liner comprising:
lining a surface of a black liquor gasifier which operates in an aqueous environment that is subject to operating pressures of black liquor gasification and wear by an alkali environment and/or an alkaline environment with a refractory composition comprising greater than 70 percent by weight of a refractory aggregate consisting essentially of a calcium hexa aluminate clinker having the formula CA 6 , wherein C is equal to calcium oxide, wherein A is equal to aluminum oxide, and wherein said hexa aluminate clinker has from zero to less than about fifty weight percent C 12 A 7 , and wherein greater than 98 weight percent of said calcium hexa aluminate clinker having a particle size ranging from −20 microns to +3 millimeters, for forming a liner of said surface prior to contacting said surface with at least one of an alkali material, and an alkaline material, or combinations of said alkali and said alkaline materials, and
providing said liner wherein said refractory composition has a surface that is devoid of thermal expansive glass phases when contacted with said alkali and/or alkaline environments at temperatures below 1830° C.
2. The method of claim 1 including contacting said lined surface with at least one said alkali material, said alkaline material, or combinations thereof.
3. The method of claim 1 including wherein said lined surface is resistant to chemical wear by said alkali material and/or said alkaline material.
4. The method of claim 3 including contacting said lined surface with at least one of said alkali material, said alkaline material, and combinations thereof, at temperatures ranging from about −20 degrees Centigrade to up to but not including about 1830 degrees Centigrade.
5. The method of claim 1 including wherein said gasifier is a gasifier of the type employed in the paper industry.
6. The method of claim 1 including wherein said vessel is employed in the paper industry.
7. The method of claim 1 including wherein said refractory composition comprises a calcium aluminate cement.
8. The method of claim 1 including wherein said refractory composition comprises an alumina.
9. The method of claim 1 including wherein said refractory composition comprises a surfactant.
10. The method of claim 1 including wherein said refractory composition comprises one or more sized fractions of said CA6 clinker.
11. The method of claim 1 including wherein said lined surface functions as a refractory lining.
12. The method of claim 1 including wherein said lined surface functions as a chemical barrier that is substantially resistant to attack by at least one or more of said alkali material, alkaline material, and combinations thereof.