Lignocellulose-based anion-adsorbing medium (LAM) and process for making and using same for the selective removal of phosphate and arsenic anionic contaminants from aqueous solutions
A lignocellulose-based anion-adsorbing medium (LAM) and process for making and using same for selectively removing phosphates and arsenic contaminants from aqueous solutions is disclosed. Making the LAM comprises (a) dissociating cations such as Fe and Al, from their counterions by adding a chemical compound containing said cations to water and acidifying; (b) pelletizing a lignocellulose; (c) adsorbing the cations to the lignocellulose by bringing the lignocellulose into contact with the solution of step (a) and incubating; and, (d) exposing the lignocellulose of step (c) to an alkaline fixing agent to replace hydrogens (H) of the hydroxyl groups of the lignocellulose with the adsorbed cations to produce the LAM with a positive charge. The LAM may be used to selectively and cost-effectively remove phosphate and arsenic contaminants from aqueous solutions by retaining them at the Fe or Al on the LAM.
1. A process for treating a contaminated aqueous solution to remove one or more phosphate anionic contaminants therefrom, comprising:
a. contacting the contaminated aqueous solution with a lignocellulose-based anion-adsorbing medium (LAM), wherein the LAM has been formed by the steps of:
i. dissociating cations selected from the group consisting of Fe, Al and Ca, from their counterions by adding a chemical compound containing said cations to water and acidifying;
ii. pelletizing a lignocellulose having hydroxyl groups (—OH);
iii. adsorbing the cations to a lignocellulose having hydroxyl groups (—OH) by bringing the lignocellulose into contact with the solution of step (i) and incubating; and
iv. replacing hydrogens (H) of the hydroxyl groups of the lignocellulose with the cations to produce the LAM with a positive charge by exposing the lignocellulose of step (iii) to an alkaline fixing agent; and,
b. recovering a treated aqueous solution with reduced content of the phosphate anionic contaminants.
2. The method of claim 1 , further comprising regenerating the LAM after its contact with the contaminated aqueous solution by treating the LAM with an alkaline solution to remove the phosphate anionic contaminants from the LAM to which the phosphate anionic contaminants have been adsorbed, and subsequently neutralizing the LAM with an acid to prepare it for reuse.
3. The method of claim 1 , wherein the lignocellulose is selected from the group consisting of wood, paper, and cotton.