Process for producing polystyrene foam particles having a high density
A process for producing polystyrene foam particles having a bulk density in the range from 40 to 400 g/l by extrusion of a polystyrene melt comprising carbon dioxide and/or water as blowing agent through a nozzle and underwater pelletization, wherein the underwater pelletization is carried out at a pressure in the range 1-30 bar.
1. A process for producing polystyrene foam particles by extrusion of a polystyrene melt comprising carbon dioxide and/or water as blowing agent through a nozzle and underwater pelletization, wherein the underwater pelletization is carried out via variable counterpressure at a pressure in the range 2-12 bar to set the bulk density of the polystyrene foam particles in the range from 40 to 400 g/l,
wherein no further blowing agents, solubilizers or emulsifiers are added to the polystyrene melt.
2. The process according to claim 1 , wherein 1-5% by weight, based on the polystyrene melt, of carbon dioxide or water is used as blowing agent.
3. The process according to claim 1 , wherein the polystyrene foam particles have a bulk density in the range from 50 to 300 g/l.
4. The process according to claim 1 , wherein from 5 to 30% by weight, based on the melt, of a filler selected from the group consisting of as talc, chalk, kaolin, aluminum hydroxide, magnesium hydroxide, aluminum nitrite, aluminum silicate, barium sulfate, calcium carbonate, calcium sulfate, silica, quartz flour, Aerosil, alumina, and wollastonite, or a mixture thereof, are added to the polystyrene melt.
5. The process according to claim 4 , wherein the filler has a mean particle diameter in the range from 2 to 50 micrometer.
6. The process according to claim 2 , wherein the polystyrene foam particles have a bulk density in the range from 50 to 300 g/l.
7. The process according to claim 2 , wherein from 1 to 50% by weight, based on the melt, of a filler are added to the polystyrene melt.
8. The process according to claim 3 , wherein from 1 to 50% by weight, based on the melt, of a filler are added to the polystyrene melt.
9. The process according to claim 1 , wherein 1-5% by weight, based on the polystyrene melt, of carbon dioxide and water is used as blowing agent and no further blowing agents are used.
10. The process according to claim 1 , wherein from 5 to 30% by weight, based on the melt, of a filler are added to the polystyrene melt.