Synthesis of water soluble non-toxic nanocrystalline quantum dots and uses thereof
An economic, direct synthetic method for producing water soluble ZnS QDs that are ready for bioconjugation is provided. The method can produce aqueous ZnS QDs with emission wavelengths varying from 400 nm to 700 nm. Highly luminescent metal sulfide (MS) QDs are produced via an aqueous synthesis route. MS QDs are capped with thiol-containing charged molecules in a single step. The resultant MS QDs exhibit the distinctive excitonic photoluminescence desired of QDs and can be fabricated to avoid undesirable broadband emissions at higher wavelengths. The aqueous ZnS QDs are stable in biological fluids over a long period of time. In addition, non-toxic ZnS QDs have been produced with good photoluminescence properties.
1. Zinc sulfide quantum dots comprising a component consisting essentially of zinc sulfide, which component is capped with at least one thiol-capping group selected from the group consisting of 3-mercaptopropionic acid group, a 3-mercaptopropyltrimethoxysilane group and a mixture thereof, wherein a molar ratio of thiol-capping groups to metal in the quantum dots is about 1.5-3, said quantum dots having an emission wavelength of from about 400-700 nm.
2. Zinc sulfide quantum dots as claimed in claim 1 , wherein the emission wavelength is from about 400-500 nm.
3. Zinc sulfide quantum dots as claimed in claim 1 , wherein the emission wavelength is from about 410-440 nm.
4. Zinc sulfide quantum dots as claimed in claim 1 , wherein the quantum yield of the quantum dots is at least about 15%, using Rhodamine 101 as a standard of 100%.
5. Zinc sulfide quantum dots as claimed in claim 1 , wherein the quantum yield of the quantum dots is at least 25%, using Rhodamine 101 as a standard of 100%.
6. Zinc sulfide quantum dots as claimed in claim 1 , wherein the quantum yield of the quantum dots is at least 30%, using Rhodamine 101 as a standard of 100%.
7. Zinc sulfide quantum dots as claimed in claim 1 , wherein the quantum yield of the quantum dots is at least 75%, using Rhodamine 101 as a standard of 100%.
8. Zinc sulfide quantum dots as claimed in claim 1 , having a particle size of from about 2 to about 10 nm.
9. Zinc sulfide quantum dots as claimed in claim 1 , having a particle size of from about 4 to about 6 nm.
10. Zinc sulfide quantum dots as claimed in claim 1 , having a particle size of from about 4.5 to about 5.5 nm.
11. Zinc sulfide quantum dots as claimed in claim 1 , wherein the thiol-capping groups comprise 3-mercaptopropionic acid groups.
12. Zinc sulfide quantum dots as claimed in claim 1 , wherein the thiol-capping groups comprise 3-mercaptopropyltrimethoxysilane groups.
13. Zinc sulfide quantum dots as claimed in claim 1 , wherein the thiol-capping groups comprise both 3-mercaptopropyltrimethoxysilane groups and 3-mercaptopropionic acid groups.
14. Zinc sulfide quantum dots as claimed in 13 , wherein the ratio of 3-mercaptopropyltrimethoxysilane groups to Zinc to sulfide is from about 0.125:4:1 to about 12:4:1.