Transparent mold made of a polyamide molding material
The invention is directed to a transparent mold made of a polyamide molding material containing at least one polyamide formed from at least one diamine selected from the group of hexamethylene diamine (HMDA), bis-(4-amino-3-methylcyclohexyl)methane (MACM) and/or bis-(4-amino-cyclohexyl)methane (PACM) as well as from at least one dicarboxylic acid selected from the group of isophthalic acid (IPS), terephthalic acid (TPS) and/or dodecanedioic acid (DDS) or from the aforementioned diamines and dicarboxylic acids in combination with lactams and/or α-/ω-amino acids.
1. Transparent mold, made of a polyamide molding material, containing at least one polyamide and/or polyamide blends with a light transmission of at least 75% at a layer thickness of 2 mm, measured in accordance with ASTM D 1003 as well as a resistance in the bending test with fixation of at least 60,000 measurement cycles, measured in accordance with ISO 178 with a special test piece, wherein the at least one polyamide is formed from diamines, which diamines are hexamethylene diamine (HMDA), bis-(4-amino-3-methylcyclohexyl) methane (MACM) and bis-(4-amino-cyclohexyl) methane (PACM) as well as from at least one dicarboxylic acid selected from the group consisting of isophthalic acid (IPS) and terephthalic acid (TPS) or from the aforementioned diamines and dicarboxylic acids in combination with lactams and/or α-/ω-amino acids.
2. Mold according to claim 1 , wherein the at least one polyamide and/or polyamide blends is formed relating to 100 mol-% diamine from
a) Approx. 39 mol-% MACM and
b) Approx. 52 mol-% HMDA and
c) Approx. 9 mol-% PACM as well as relating to 100 mol-% of the dicarboxylic acids from
d) Approx. 50 mol-% IPS and
e) Approx. 50 mol-% TPS.
3. Mold according to claim 1 , wherein up to 10 wt.-% in terms of the total weight of the polyamide molding material is made of lactam and/or an α-/ω- amino acid.
4. Mold according to claim 3 , wherein approx. 4.6 wt.-% in terms of the total weight of the polyamide molding material is made of a lactam and/or an α-/ω- amino acid.
5. Mold according to claim 4 , wherein approx. 3 wt.-% in terms of the total weight of the polyamide molding material is made of a lactam and/or an α-/ω- amino acid.
6. Mold according to claim 1 , wherein the lactam and/or the α-/ω- amino acid is LC 11, LC 12, α-/ω- amino undecane acid and/or α-/ω-amino dodecane acid.
7. Mold according to claim 1 , wherein the dicarboxylic acids are replaced by naphthalene dicarboxylic acid for up to a maximum of half of their molar content.
8. Mold according to claim 1 , wherein the mold has a light transmission of at least 88% at a layer thickness of 2 mm, measured in accordance with ASTM D 1003.
9. Mold according to claim 1 , wherein the resistance in the alternating bend test with fixation is at least 75,000 measurement cycles measured in accordance with ISO 178 with a special test piece.
10. Mold according to claim 1 , wherein the mold has a refractive index of 1.490-1.75.
11. Mold according to claim 1 , wherein the mold has an Abbe number of at least 25.
12. Mold according to claim 1 , wherein the mold is an optical mold.
13. Mold according to claim 12 , wherein the optical mold is a lens.
14. Mold according to claim 1 , wherein the mold is colored.
15. Mold according to claim 1 , wherein the mold has an optically active coating and/or a protective coating.
16. Mold according to claim 1 , wherein the at least one polyamide contains additives selected from the group consisting of condensation catalysts, chain regulators, defoaming agents, stabilizers, lubricants, dyes, photochrome additives, antistatics, demolding agents, optical brighteners, natural phyllo silicates, synthetic phyllo silicates or mixtures of the named additives.