Radiation curable and jettable ink compositions
Radiation curable and jettable ink compositions comprise ethylenically unsaturated oligomer and an ethylenically unsaturated monofunctional monomer. The compositions may optionally include additional ethylenically unsaturated polyfunctional component and/or chain transfer agent. The compositions have a viscosity at 25° C. of not greater than about 70 cPs and are radiation curable to form a cured ink having an elongation of at least 150%.
1. A radiation curable and jettable ink composition, comprising the following components:
(a) an oligomer containing a mono-ethylenically unsaturated radiation curable functional group;
(b) an ethylenically unsaturated monofunctional monomer;
(c) optionally, an oligomer or a monomer each said oligomer or monomer containing ethylenically unsaturated polyfunctional groups; and
(d) optionally, a chain transfer agent;
wherein components (a) and (c) combined by weight is less than components (b) and (d) combined by weight and further wherein the ink composition is (1) substantially free of solvent, (2) has a viscosity at 25° C. of not greater than about 70 cPs, and (3) when cured by radiation forms an ink having an elongation of at least about 150%.
2. The ink composition of claim 1 , having a viscosity at 25° C. of not greater than about 50 cPs.
3. The ink composition of claim 1 , comprising from about 5 to about 35 wt % of the mono-ethylenically unsaturated oligomer and any optional oligomer or monomer containing ethylenically unsaturated polyfunctional groups combined, and from about 25 to about 80 wt % of the ethylenically unsaturated monofunctional monomer and any optional chain transfer agent combined.
4. The ink composition of claim 1 , wherein the mono-ethylenically unsaturated oligomer comprises an aromatic mono-acrylate.
5. The ink composition of claim 4 further comprises a polyfunctional acrylate oligomer.
6. The ink composition of claim 5 , wherein the polyfunctional acrylate oligomer comprises an aliphatic polyester urethane diacrylate oligomer.
7. The ink composition of claim 6 further comprises an additional polyfunctional ethylenically unsaturated oligomer.
8. The ink composition of claim 5 further comprising an amine diacrylate oligomer.
9. The ink composition of claim 5 further comprising a hexafunctional acrylate.
10. The ink composition of claim 9 , wherein the hexafunctional acrylate comprises a silicone acrylate.
11. The ink composition of claim 1 , wherein the ethylenically unsaturated monofunctional monomer comprises a monofunctional acrylate monomer or a monofunctional acrylate monomer containing a cyclic group, wherein the cyclic group is aliphatic or aromatic and may contain one or more homo or heterocyclic ring structures.
12. The ink composition of claim 11 , wherein the monofunctional acrylate monomer comprises isobornyl acrylate.
13. The ink composition of claim 1 , the chain transfer agent is present and is selected from an acetoacetate, a thiol, an amine, a mercapto-modified silicone, and combinations thereof.
14. The ink composition of claim 1 , wherein the composition is substantially free of non-reactive oligomers.
15. The ink composition of claim 1 , wherein the composition is substantially free of non-reactive oligomers having a molecular weight of greater than 10,000 g/mole.
16. The ink composition of claim 1 , wherein the composition is free of acrylic polymer or co-polymer having an acid number of below about 20.
17. The radiation curable and jettable ink composition of claim 1 further comprising a colorant.
18. A radiation curable and jettable ink composition for printing onto a substrate which is then thermoformed, said ink composition consisting essentially of the following components:
(a) from about 5 wt % to about 30 wt % of an oligomer containing a mono-ethylenically unsaturated radiation curable functional group;
(b) from about 25 wt % to about 80 wt % of an ethylenically unsaturated monofunctional monomer;
(c) from about 1 wt % to about 15 wt % of an oligomer or a monomer, each said oligomer or monomer containing ethylenically unsaturated polyfunctional groups; and
(d) from about 0 wt % to about 25 wt % of a chain transfer agent,
wherein the combined weight amount of the components (a) and (c) is less than the combined weight amount of the components (b) and (d) and further wherein the ink composition (1) is substantially free of solvent, (2) is substantially free of acrylic polymers or co-polymers having an acid number below about 20, (3) has a viscosity at 25° C. of not greater than about 50cPs, and (4) when cured by radiation forms an ink having an elongation of at least about 150%.
19. The ink composition of claim 18 , having a viscosity at 25° C. of not greater than about 30 cPs.
20. An article comprising a substrate and the cured ink composition of claim 1 .
21. The radiation curable and jettable ink composition of claim 18 further consisting essentially of from about 0.01 wt. % to about 25 wt. % of a colorant.
22. The radiation curable and jettable ink composition of claim 1 further wherein the composition has a surface tension at 25° C. of less than about 40 dynes/cm.