High strength and sagging resistant fin material
The present invention provides a method for producing AlMn strip or sheet for making components by brazing, as well as the products obtained by said method. In particular this method is related to fin materials used in heat exchangers. The fins can be delivered with or without a cladding depending on application. Rolling slabs are produced from a melt which contains 0.3-1.5% Si, ≤0.5% Fe, ≤0.3% Cu, 1.0-2.0% Mn, ≤0.5% Mg, ≤4.0% Zn, ≤0.3% each of elements from group IVb, Vb, or VIb elements, and unavoidable impurity elements, as well as aluminum as the remainder in which the rolling slabs prior to hot rolling are preheated at a preheating temperature of less than 550° C., preferably between 400 and 520° C., more preferably between 450 and 520° C. to control the number and size of dispersoid particles, and the preheated rolling slab is hot rolled into a hot strip. The strip is thereafter cold rolled into a strip with a total reduction of at least 90%, and the cold rolled strip is heat treated to obtain a 0.2% proof stress value that is 50-90% of its proof stress value in the as cold rolled condition to a proof stress value in the range between 100 and 200 MPa. The strip may alternatively be produced by twin-roll strip casting. The composition of the melt tailors the microstructure development during the complete processing to give the desired post braze properties and performance during brazing in combination with adequate delivery properties of the strip. In particular the high post braze strength combined with a good sagging resistance and low susceptibility to liquid core penetration during brazing, as well as a relatively good formability in the delivery condition prior to fin forming.
1. A method of producing a sagging resistant strip having a final gauge for incorporation into a component by brazing, comprising
a) casting a melt containing:
0.3-1.5 wt % Si,
<0.5 wt % Fe,
<0.3 wt % Cu,
1.0-2.0 wt % Mn,
<0.5 wt % Mg,
<4.0 wt % Zn,
<0.3 wt % each of dispersoid forming elements from group IVb, Vb, or VIb, and
unavoidable impurity elements, each at most 0.05 wt %, in a total amount of at most 0.15 wt %,
the rest aluminium, to obtain an ingot,
b) preheating the resulting ingot at a temperature of less than 550° C. so as to form dispersoid particles,
c) hot rolling to obtain a strip,
d) cold rolling the strip obtained in step c) to the final gauge with a total reduction of at least 90% and without intermediate annealing giving recrystallisation of the strip alloy, resulting in a cold rolled strip having a first proof stress value,
e) heat treating the cold rolled strip from step d) with the final gauge to the delivery temper to soften the material by a tempering without any recrystallisation of the strip alloy to obtain a strip having a second proof stress value which is 10-50% lower than the first proof stress value obtained directly after cold rolling in step d), and lying in the absolute proof stress range of 100-200 MPa.
2. A method according to claim 1 , comprising cold rolling to a reduction of at least 97.5%.
3. A method according to claim 1 , the melt containing:
0.5-1.1 wt % Si,
<0.3 wt % Fe,
<0.1 wt % Cu,
1.3-1.8 wt Mn,
<0.1 wt % Mg,
0.05-0.2 wt % Zr.
4. A method according to claim 3 , wherein the melt includes 1.4-1.7 wt % Mn.
5. A method according to claim 3 , wherein the melt includes between 0.1 and 0.2 wt % Zr.
6. A method according to claim 1 , the melt containing between 0.5 and 2.8 wt % Zn.
7. A method according to claim 1 , the melt containing <0.009 wt % Sn.
8. A method according to claim 1 , comprising controlling the preheating step so that a strip is produced having in the delivery temper a dispersoid particle density in the range between 1×10 6 and 20×10 6 particles/mm 2 of particles of particles having a diameter in the range of 50-400 nm.
9. A method according to claim 8 , including controlling the preheating step so that the strip is produced having in the delivery temper the dispersoid particle density in the range between 1.3×10 6 and 10×10 6 particles/mm 2 .
10. A method according to claim 8 , including controlling the preheating step so that the strip is produced having in the delivery temper the dispersoid particle density in the range between 1.4×10 6 and 7×10 6 particles/mm 2 .
11. A sagging resistant strip according to claim 1 , having a final thickness of the strip less than 0.2 mm.
12. A method according to claim 11 , wherein the final thickness of the strip is less than 0.15 mm.
13. A method according to claim 11 , wherein the final thickness of the strip is less than 0.10 mm.
14. A method according to claim 1 , comprising controlling the process parameters so that a strip is produced having after brazing a 0.2% proof stress value of at least 60 MPa.
15. A method according to claim 14 , including controlling the process parameters so that the strip is produced having after brazing the 0.2% proof stress value of at least 70 MPa.
16. A method according to claim 1 , wherein the sagging resistant strip has a sagging resistance of <35 mm when measured on a 0.10 mm thick strip.
17. A method according to claim 16 , wherein the sagging resistance is <30 mm when measured on the 0.10 mm thick strip.
18. A method according to claim 16 , wherein the sagging resistance is <25 mm when measured on the 0.10 mm thick strip.
19. A method according to claim 1 , wherein the sagging resistant strip has a sagging resistance of <20 mm when measured on a 0.10 mm thick strip.
20. A method according to claim 19 , wherein the sagging resistance is <15 mm when measured on the 0.10 mm thick strip.
21. A method according to claim 1 , wherein the melt includes <0.3 wt % Mg.
22. A method according to claim 1 , wherein step b) includes preheating the resulting ingot at a temperature of 400-520° C.
23. A method according to claim 1 , wherein step b) includes preheating the resulting ingot at a temperature of 450-520° C.
24. A method according to claim 1 , wherein step b) includes preheating the resulting ingot at a temperature of 470 up to 520° C.
25. A method according to claim 1 , including cold rolling the strip obtained in step c) with the total reduction >95%.
26. A method according to claim 1 , wherein the second proof stress value is 15-40% lower than the first proof stress value obtained directly after cold rolling in step d).
27. A method according to claim 1 , wherein the second proof stress value is in the range of 120-180 MPa.
28. A method according to claim 1 , wherein the second proof stress value is in the range of 140-180 MPa.
29. A method of producing a sagging resistant strip having a final gauge for incorporation into a component by brazing, comprising
a) twin-roll strip casting a melt comprising:
0.3-1.5 wt % Si,
<0.5 wt % Fe,
<0.3 wt % Cu
1.0-2.0 wt % Mn,
<0.5 wt % Mg,
<4.0 wt % Zn,
<0.3 wt % each of dispersoid forming elements from group IVb, Vb, or VIb, and
unavoidable impurity elements, each at most 0.05 wt %, in a total amount of at most 0.15 wt %,
the rest aluminium, to obtain an as-cast strip,
b) cold rolling the as-cast strip to form an intermediate gauge material,
c) annealing the intermediate gauge sheet material to form dispersoid particles,
d) cold rolling the intermediate gauge article to a finstock material of final gauge with a rolling reduction of at least 60% and without intermediate annealing giving recrystallisation of the strip alloy, resulting in a finstock material having a first proof stress value,
e) heat treating the finstock material having the final gauge to the delivery temper to soften the material by a tempering without any recrystallisation of the strip alloy to obtain a strip having a second proof stress value which is 10-50% lower than that obtained directly after cold rolling in step d), and lying in the proof stress range of 100-200 MPa.
30. A method according to claim 29 , comprising controlling the intermediate annealing step so that a strip is produced having in the delivery temper a dispersoid particle density in the range between 1×10 6 and 20×10 6 particles/mm 2 of particles of particles having a diameter in the range of 50-400 nm.
31. A method according to claim 30 , including controlling the intermediate annealing step so that the strip is produced having in the delivery temper the dispersoid particle density in the range between 1.3×10 6 and 10×10 6 particles/mm 2 .
32. A method according to claim 30 , including controlling the intermediate annealing step so that the strip is produced having in the delivery temper the dispersoid particle density in the range between 1.4×10 6 and 7×10 6 particles/mm 2 .
33. A method according to claim 29 , comprising before step b) cladding the ingot or finstock material with at least one additional layer.
34. A method according to claim 33 , where the at least one additional layer consists of a braze alloy.
35. A method according to claim 33 , where the at least one additional layer consists of a commercially pure aluminium alloy.
36. A method according to claim 33 , where the at least one additional layer consists of an aluminium alloy comprising 0.6-6.5 wt % Si.
37. A method according to claim 29 , wherein the melt includes <0.3 wt % Mg.
38. A method according to claim 29 , including cold rolling the intermediate gauge article to the finstock material of final gauge with the rolling reduction of at least 75%.
39. A method according to claim 29 , wherein the second proof stress value is 15-40% lower than that obtained directly after cold rolling in step d).
40. A method according to claim 29 , wherein the second proof stress value is in the range of 120-180 MPa.
41. A method according to claim 29 , wherein the second proof stress value is in the range of 120-160 MPa.
42. A method of producing a sagging resistant strip, comprising a first processing stage and a second processing stage, wherein the first processing stage includes the steps of:
a) forming an ingot by casting a melt containing:
0.3-1.5 wt % Si,
<0.5 wt % Fe,
<0.3 wt % Cu,
1.0-2.0 wt % Mn,
<0.5 wt % Mg,
<4.0 wt % Zn,
<0.3 wt % each of dispersoid forming elements from group IVb, Vb, or VIb, and
unavoidable impurity elements, each at most 0.05 wt %, in a total amount of at most 0.15 wt %,
the rest aluminium,
b) preheating the ingot at a temperature of less than 550° C. to form dispersoid particles in a microstructure of the ingot, and
c) after preheating, hot rolling the ingot to obtain a strip, and wherein the second processing stage consists of the steps of:
d) cold rolling the strip obtained in step c) to final gauge with a total reduction of at least 90% and without intermediate annealing giving recrystallisation of the strip alloy, resulting in a cold rolled strip having a first proof stress value, and
e) heat treating the cold rolled strip from step d) to the delivery temper to soften the material by a tempering without any recrystallisation of the strip alloy to obtain a strip having a second proof stress value which is 10-50% lower than the first proof stress value obtained directly after cold rolling in step d), and lying in the absolute proof stress range of 100-200 MPa,
wherein all rolling operations to reduce a thickness of the hot rolled strip obtained in step c) occur in the second processing stage.
43. A method of producing a sagging resistant strip, consisting of:
a) twin-roll strip casting a melt comprising:
0.3-1.5 wt % Si,
<0.5 wt % Fe,
<0.3 wt % Cu
1.0-2.0 wt % Mn,
<0.5 wt % Mg,
<4.0 wt % Zn,
<0.3 wt % each of dispersoid forming elements from group IVb, Vb, or VIb and
unavoidable impurity elements, each at most 0.05 wt %, in a total amount of at most 0.15 wt %,
the rest aluminium, to obtain an as-cast strip,
b) optionally cladding the as-cast strip with at least one additional layer,
c) cold rolling the as-cast strip from step a) or step b) to form an intermediate gauge material
d) annealing the intermediate gauge sheet material to form dispersoid particles,
e) cold rolling the annealed intermediate gauge sheet material with a rolling reduction of at least 60% and without intermediate annealing giving recrystallisation of the strip alloy to form a finstock material having a final gauge and first proof stress value, and
f) heat treating the finstock material having the final gauge to a delivery temper to soften the material by a tempering without any recrystallisation of the strip alloy, wherein the heat treated finstock material has a second proof stress value which is 10-50% lower than the first proof stress value, and the second proof stress value is 100-200 MPa.
44. A method of producing a sagging resistant strip having a final gauge for incorporation into a component by brazing, comprising
a) casting a melt containing:
0.3-1.5 wt % Si,
<0.5 wt % Fe,
<0.3 wt % Cu,
1.0-2.0 wt % Mn,
<0.5 wt % Mg,
0.5-2.8 wt % Zn,
<0.3 wt % each of dispersoid forming elements from group IVb, Vb, or VIb, and
unavoidable impurity elements, each at most 0.05 wt %, in a total amount of at most 0.15 wt %,
the rest aluminium, to obtain an ingot,
b) preheating the resulting ingot at a temperature of less than 550° C. so as to form dispersoid particles,
c) hot rolling to obtain a strip,
d) cold rolling the strip obtained in step c) to the final gauge with a total reduction of at least 90% and without intermediate annealing giving recrystallisation of the strip alloy, resulting in a cold rolled strip having a first proof stress value,
e) heat treating the cold rolled strip from step d) with the final gauge to the delivery temper to soften the material by a tempering without any recrystallisation of the strip alloy to obtain a strip having a second proof stress value which is 10-50% lower than the first proof stress value obtained directly after cold rolling in step d), and lying in the absolute proof stress range of 100-200 MPa.
45. A method of producing a sagging resistant strip having a final gauge for incorporation into a component by brazing, comprising
a) twin-roll strip casting a melt comprising:
0.3-1.5 wt % Si,
<0.5 wt % Fe,
<0.3 wt % Cu
1.0-2.0 wt % Mn,
<0.5 wt % Mg,
0.5-2.8 wt % Zn,
<0.3 wt % each of dispersoid forming elements from group IVb, Vb, or VIb, and
unavoidable impurity elements, each at most 0.05 wt %, in a total amount of at most 0.15 wt %,
the rest aluminium, to obtain an as-cast strip,
b) cold rolling the as-cast strip to form an intermediate gauge material,
c) annealing the intermediate gauge sheet material to form dispersoid particles,
d) cold rolling the intermediate gauge article to a finstock material of final gauge with a rolling reduction of at least 60% and without intermediate annealing giving recrystallisation of the strip alloy, resulting in a finstock material having a first proof stress value,
e) heat treating the finstock material having the final gauge to the delivery temper to soften the material by a tempering without any recrystallisation of the strip alloy to obtain a strip in a tempered state of H22, H24 or H26 having a second proof stress value which is 10-50% lower than that obtained directly after cold rolling in step d), and lying in the proof stress range of 100-200 MPa.