Polyimide-titania hybrid materials, their preparation, and film prepared from the materials
The present invention relates to polyimide-titania hybrid thin film, which possesses relatively good surface planarization, excellent thermal properties (400<Td<550° C.), tunable refractive index (1.571<n<1.993), and highly optical transparency in the visible range. The present invention also relates to a method for preparing the polyimide-titania hybrid materials, which comprises producing a polyimide containing pendent and/or terminal carboxylic acid, coordinating the carboxylic acid with titanium of titanium alkoxide and sol-gel reacting of titanium alkoxide, to enhance the interaction between polyimide and titania and produce the polyimide-titania hybrid materials without macrophase separation. The present polyimide-titania hybrid materials are useful to produce the thin film having the above features.
1. A method for preparing polyimide-titania hybrid material, which comprises the steps of:
(a) reacting an aromatic dianhydride monomer with an aromatic diamine monomer and optionally carboxylic acid-substituted aromatic diamine monomer in a mole ratio (x/y) of (moles of aromatic dianhydride)(in terms of x)/(total moles of aromatic diamine and carboxylic acid-substituted aromatic diamine)(in terms of y) is more than 1 to subject the dianhydride to a ring-opening reaction to obtain polyamic acid having a terminal anhydride group;
(b) further subjecting the polyamic acid having a terminal anhydride group from step (a) to ring-opening by adding aniline and/or aminobenzoic acid to obtain a polyamic acid having pendent and/or terminal carboxylic acid group, wherein the amount of the aniline and/or aminobenzoic acid is 2×(x−y) in total moles;
(c) subjecting the polyamic acid having pendent and/or terminal carboxylic acid group from step (b) to imidization (cyclization) to obtain a polyimide having pendent and/or terminal carboxylic acid group; and
(d) reacting the polyimide having pendent and/or terminal carboxylic acid group from step (c) with titanium alkoxide to coordinate the carboxylic acid group with titanium atom, then subjecting to hydrolysis and condensation to obtain the polyimide-titania hybrid material.
2. The method according to claim 1 , wherein the polyimide having pendent and/or terminal carboxylic acid group from step (c) has an acid number in a range of from 20 mg KOH/g to 200 mg KOH/g.
3. The method according to claim 1 , wherein the step (a) is carried out in the absence of carboxylic acid-substituted aromatic diamine and the step (b) is carried in the presence of at least the aminobenzoic acid.
4. The method according to claim 1 , wherein the step (a) is carried out in the presence of carboxylic acid-substituted aromatic diamine and the step (b) is carried in the presence of the aniline and/or aminobenzoic acid.
5. The method according to claim 1 , wherein the aromatic dianhydride is one or more compounds selected from the group consisting of 4,4′-(Hexafluoroisopropylidene) diphthalic anhydride (6FDA), pyromellitic dianhydride, 4,4′-oxy-diphthalic anhydride, 3,3′,4,4′-biphenyltetracarboxylic dianhydride, 3,3,4,4′-benzophenonetetracarboxylic dianhydride, ethylenetetracarboxylic dianhydride, butanetetracarboxylic dianhydride, cyclopentane-tetracarboxylic dianhydride, 2,2′,3,3′-benzophenonetetracarboxylic dianhydride, 2,2′,3,3′-biphenyl-tetracarboxylic dianhydride, 2,2-bis-(3,4-dicarboxyphenyl)propane dianhydride, 2,2-bis(2,3-dicarboxyphenyl)propane dianhydride, bis(3,4-dicarboxyphenyl)ether dianhydride, bis-(3,4-dicarboxyphenyl)sulfone dianhydride, 1,1-bis(2,3-dicarboxyphenyl)ethane dianhydride, bis(2,3-dicarboxyphenyl)methane dianhydride, bis(3,4-dicarboxyphenyl)-methane dianhydride, 4,4′-(p-phenylenedioxy)diphthalic dianhydride, 4,4′-(m-phenylenedioxy)diphthalic dianhydride, 2,3,6,7-naphthalene-tetracarboxylic dianhydride, 1,4,5,8-naphthalenetetracarboxylic dianhydride, 1,2,5,6-naphthalenetetracarboxylic dianhydride, 1,2,3,4-benzene-tetracarboxylic dianhydride, 3,4,9,10-perylenetetracarboxylic dianhydride, 2,3,6,7-anthracenetetracarboxylic dianhydride, and 1,2,7,8-phenanthrenetetracarboxylic dianhydride.
6. The method according to claim 1 , wherein the aromatic diamine is one or more compounds selected from the group consisting of 4,4′-(hexafluoroisopropylidene) dianiline (6FpDA), p-phenylene diamine, 4,4-oxydianiline, 1,3-bis(4-aminophenoxy)benzene, 1,3-bis(3-aminophenoxy)benzene, 2,2-bis[4-(4-aminophenoxy)phenyl]propane, bis[4-(4-aminophenoxy)phenyl]sulfone, 4,4′-bis(4-aminophenoxy)-3,3′-dihydroxybiphenyl, bis[4-(3-aminophenoxy)phenyl]methane, 1,1-bis-[4-(3-aminophenoxy)phenyl]ethane, 1,2-bis[4-(3-aminophenoxy)phenyl]ethane, 2,2-bis[4-(3-aminophenoxy)phenyl]propane, 2,2′-bis-[4-(3-aminophenoxy)phenyl]butane, 2,2-bis[4-(3-amino-phenoxy)phenyl]-1,1,1,3,3,3-hexafluoropropane, 4,4′-bis(3-aminophenoxy)biphenyl, bis[4-(3-aminophenoxy)phenyl]ketone, bis[4-(3-aminophenoxy)phenyl]sulfide, bis[4-(3-aminophenoxy)phenyl]sulfoxide, bis[4-(3-aminophenoxy)phenyl]sulfone, and bis[4-(3-aminophenoxy)phenyl]ether.
7. The method according to claim 1 , wherein the carboxylic acid-substituted aromatic dianhydride is 3,5-diaminobenzoic acid.
8. The method according to claim 1 , wherein the steps (a) and (b) are carried out at a temperature of from ambient temperature to 90° C.
9. The method according to claim 1 , wherein the step (c) is carried out at a temperature of from 120° C. to 200° C.
10. The method according to claim 1 , wherein the coordination in the step (d) is carried out under the condition that mole ratio of [Ti]/[COOH] is more than 3.
11. The method according to claim 10 , wherein the coordination in the step (d) is carried out under the condition that mole ratio of [Ti]/[COOH] is more than 8.
12. The method according to claim 1 , wherein the condensation with titanium alkoxide in the step (d) is carried out in the presence of alkanol.
13. The method according to claim 12 , wherein the alkanol has the carbon atom numbers the same as the alkoxide in the titanium alkoxide.