Carbon based field emission cathode and method of manufacturing the same
According to example embodiments, a method for manufacturing a field emission cathode includes providing a liquid compound comprising a liquid phenolic resin and at least one of a metal salt and a metal oxide arranging a conductive cathode support in a vicinity of the liquid compound, and heating the liquid compound. Heating the liquid compound transforms the liquid compound into a solid compound foam.
1. A method, for manufacturing a field emission cathode, comprising:
providing a liquid compound comprising a liquid phenolic resin and at least one of a metal salt and a metal oxide;
arranging a conductive cathode support in a vicinity of said liquid compound
arranging the conductive cathode support and the liquid compound in an enclosed container;
heating said liquid compound, thereby forming a solid compound foam, transformed from said liquid compound,
wherein the liquid compound as a result of the heating will expand in volume inside of the enclosed container to form the solid compound foam that will be provided in firm contact with the conductive cathode support and at least partly covering the conductive cathode support.
2. A method according to claim 1 , wherein the method further comprises performing a pyrolysis process on said solid compound foam at least partly covering said conductive cathode support, thereby forming a carbonized solid compound foam.
3. A method according to claim 2 , further comprising: performing a cutting action on said carbonized solid compound foam, thereby forming a carbonized solid compound foam with a plurality of sharp emission edges.
4. A method according to claim 3 , wherein said carbonized solid compound foam has a continuous cellular structure.
5. A method according to claim 1 ,
wherein said conductive cathode support is a rod,
wherein said container is a substantially cylindrical container, and
wherein the heating said liquid compound comprises substantially aligning a longitudinal centre axis of said substantially cylindrical container with a horizontal plane axis.
6. A method according to claim 5 , wherein the heating said liquid compound in said substantially cylindrical container comprises rotating said substantially cylindrical container around its substantially horizontal axis.
7. A cathode, for emitting electrons when a potential difference is applied between the cathode and an anode in a field emission device application, wherein the cathode is manufactured according to the method of claim 1 .
8. A field emission device application comprising:
a cathode manufactured according to the method of claim 1 ;
an anode;
a means for arranging said anode and said cathode in an evacuated chamber; and
control electronics.
9. A field emission device application according to claim 8 , wherein said field emission device application is one of a lighting source application and an X-ray application.
10. The method according to claim 1 , wherein
the metal salt includes an alkaline metal salt, and
the metal oxide includes an alkaline metal oxide.
11. An apparatus for manufacturing a cathode, for use in a field emission device application, comprising:
means for providing a liquid compound comprising a liquid phenolic resin and at least one of a metal, a metal salt, and a metal oxide;
means for arranging a conductive cathode support together with the liquid compound in the enclosed container, thereby arranging the conductive cathode support in the vicinity of said liquid compound, wherein the liquid compound as a result of the heating will expand in volume inside of the enclosed container to form the solid compound foam that will be provided in firm contact with the conductive cathode support and at least partly covering the conductive cathode support.