Continuous production of titanium by the metallothermic reduction of TiCl
View Patent ↗A method for production of titanium particles or other metal of interest by a metallothermic reduction reaction of TiCl 4 or other metal chloride in a reaction zone which comprises conducting the reaction in a fluidized bed reaction zone, and recycling particles to the reaction zone to build up particle size.
1. A method for the production of titanium by the metallothermic reduction reaction of TiCl 4 in gaseous state, which comprises conducting the reaction in a fluidized bed reaction zone to produce titanium particles, collecting the particles on a substrate, vibrating or flexing the substrate so that particles fall back into the reaction zone, and continuously recycling particles to the reaction zone to build up particle size.
2. The method of claim 1 , comprising withdrawing titanium particles from the reaction zone once they achieve a pre-determined size.
3. The method of claim 1 , wherein the substrate comprises a screen or sheet.
4. The method of claim 3 , wherein the screen or sheet is formed of titanium.
5. The method of claim 3 , wherein the sheet has a contoured surface.
6. The method of claim 5 , wherein the contoured surface is formed by machining or etching.
7. The method of claim 5 , wherein the sheet has a plurality of half-round columns formed in a surface thereof.
8. The method of claim 1 , wherein the particles are deposited on a substrate, and including the step of scraping the deposit from the substrate.
9. The method of claim 8 , wherein the substrate comprises a bundle of wires, and the particles are deposited on the ends of the wires.
10. The method of claim 1 , wherein the fluidized bed is pulse fluidized.
11. A method for the production of titanium which comprises reacting gaseous TiCl 4 and Mg in a molten salt reactor, wherein the titanium produced is in a molten state, and including the steps of solidifying the molten titanium by passing the molten titanium to a cooling zone, and collecting the solidified titanium from the cooling zone.
12. The method of claim 11 , and including the step of removing the solidified titanium from the cooling zone.
13. The method of claim 11 , wherein the molten salt comprises calcium fluoride.
14. The method of claim 11 , wherein MgCl 2 is produced as a by-product, and including the steps of passing the by-product MgCl 2 to electrolysis where the Mg is recovered and recycled to the molten salt reactor.
15. The method for the production of a metal of interest by metallothermic reduction reaction of a metal chloride in a gaseous state, which comprises conducting the reaction in a fluidized bed reaction zone to form particles of the metal of interest, collecting the particles on a substrate, vibrating or flexing the substrate so that particles fall back into the reaction zone, and continuously recycling particles to the reaction zone to build up particle size; wherein the metal of interest is selected from the group consisting of the chromium, hafnium, molybdenum, niobium tantalum, tungsten, vanadium and zirconium.
16. The method of claim 15 , comprising withdrawing metal particles of interest from the reaction zone once they achieve a pre-determined size.
17. The method of claim 15 , wherein the substrate comprises a screen or sheet.
18. The method of claim 17 , wherein the screen or sheet is formed of the metal of interest.
19. The method of claim 17 , wherein the sheet has a contoured surface.
20. The method of claim 19 , wherein the contoured surface is formed by machining or etching.
21. The method of claim 19 , wherein the sheet has a plurality of half-round columns formed in a surface thereof.
22. The method of claim 15 , wherein the fluidized bed is pulse fluidized.
23. The method of claim 15 , wherein the particles are deposited on a substrate, and including the step of scraping the deposit from the substrate.
24. The method of claim 23 , wherein the substrate comprises a bundle of wires, and the particles are deposited on the ends of the wires.
25. The method of claim 24 , wherein the metal of interest is produced in a molten state, and including the steps of solidifying the molten metal of interest by passing the molten metal of interest to a cooling zone, and collecting the solidified metal of interest from the cooling zone.
26. A method for the production of a metal of interest by metallothermic reduction reaction of a metal chloride in a gaseous state, which comprises reacting gaseous metal chloride and Mg in a molten salt reactor, wherein the metal of interest produced is in a molten state, and including the steps of solidifying the molten metal of interest by passing the molten metal of interest to a cooling zone and collecting the solidified metal of interest from the cooling zone, and wherein the metal of interest is selected from the group consisting of chromium, hafnium, molybdenum, niobium, tantalum, tungsten, vanadium, and zirconium.
27. The method of claim 26 , wherein the molten salt comprises calcium fluoride.
28. The method of claim 26 , wherein MgCl 2 is produced as a by-product, and including the steps of passing the by-product MgCl 2 to electrolysis where the Mg is recovered and recycled to the molten salt reactor.