Lithium silicate glass ceramic for fabrication of dental appliances
The present invention relates to preparing an improved lithium silicate glass ceramic for the manufacture of blocks for dental appliance fabrication using a CAD/CAM process. The lithium silicate material has a chemical composition that is different from those reported in the prior art including 8 to 10% of germanium dioxide in the final composition. The softening points are close to the crystallization final temperature of 800° C. indicating that the samples will support the temperature process without shape deformation. The resulting material has improved castability and higher density.
1 . A lithium silicate ceramic glass made from a composition mixture comprising:
up to about 59% wt SiO2;
up to about 20% wt Li 2 O;
up to about 10% wt GeO 2 ; and
selected amounts %wt of at least Al 2 O 3 , K 2 O, B 2 O 3 , CeO 2 and P 2 O 5 .
2 . The lithium silicate ceramic glass recited in claim 1 wherein said composition mixture also comprises one or more of the components ZrO 2 , TiO 2 , Er 2 O 3 , V 2 O 5 , MnO 2 , Tb 4 O7, Ta 2 O 5 , Dy 2 O 3 , Sm 2 O 3 , Pr 2 O 3 and Eu 2 O 3 .
3 . A lithium silicate ceramic glass made from a composition mixture comprising:
about 54.3% wt SiO 2 ;
about 15.2% wt Li 2 O; and
about 7.6% wt GeO 2 .
4 . The lithium silicate ceramic glass recited in claim 3 wherein said composition mixture also comprises at least 1.9% wt of each of Al 2 O 3 , K 2 O, P 2 O 5 , ZrO 2 , CeO 2 , Pr 2 O 3 and Sm 2 O 3 .
5 . The lithium silicate ceramic glass recited in claim 4 further comprising one or more of the following additional components TiO2, Er 2 O 3 and V 2 O 5 .
6 . The lithium silicate ceramic glass recited in claim 1 comprising a molar ratio of (SiO2+GeO2)/Li2O between 1.9 and 2.5 and SiO2/GeO2 molar ratio equal to or less than 13.