Pellets for Se encapsulation

1. A capsule pellet, consisting of:

a heart comprising at least one of selenium or a selenium compound; and

a matrix encapsulating the heart;

wherein

the matrix comprises a compressed material that does not melt at a temperature less than 1300° C. at normal pressure,

the compressed material does not contain any compound which would be a gas at a temperature less than 200° C.,

the compressed matrix material forms a eutectic product having a melting temperature in a range of 400° C. to 1800° C. at normal pressure with at least one material which is a conventional constituent of glass, and

a length of the capsule pellet in a largest dimension is at least 0.5 cm.

2. The capsule pellet according to claim 1 , wherein the at least one of selenium or a Se compound is selected from the group consisting of metallic selenium, an inorganic selenium salt, an organic selenium salt and an organic compound comprising selenium.

3. The capsule pellet according to claim 2 , wherein the selenium compound is a selenite or a selenate.

4. The capsule pellet according to claim 1 , wherein the matrix comprises at least one selected from the group of compounds consisting of SiO 2 , Na 2 O, K 2 O, Li 2 O, B 2 O 3 , CaO, MgO, BaG, ZnO, Al 2 O 3 , Fe 2 O 3 , Se, TiO 2 , CoO, MnO, Cr 2 O 3 , CeO 2 , ZrO 2 , NiO, SnO 2 , Cu 2 O, V 2 O 5 and SO 3 .

5. The capsule pellet according to claim 4 , wherein the matrix further comprises at least one material selected from the group consisting of sand, cement, dolomite and a mixture thereof.

6. The capsule pellet according to claim 1 , wherein the conventional constituent of glass with which the matrix forms an eutectic product is at least one selected from the group consisting of CaO, MgO and SiO 2 .

7. A process to manufacture the capsule pellet according to claim 1 , comprising:

dry mixing a total quantity of matrix material to obtain an initial mold mixture;

splitting the initial mold mixture into two parts;

pouring one part of the two parts of the initial mold mixture into a mold having an open cavity with an aperture with a cross section;

inserting a rod having a cross sectional dimension which is smaller than the aperture of the mold cavity into the mold to contact the initial mold mixture;

pressing the rod with the aid of a press against the initial mold mixture to solidify the initial mold mixture into a lower half of the capsule pellet;

removing the rod from the mold cavity;

depositing at least one of selenium or selenium compound in the mold cavity on a top center area of the lower half capsule pellet;

pouring the remaining part of the initial mold mixture into the mold cavity;

again inserting the rod;

pressing the rod with the aid of a press to form the capsule pellet; and

removing the capsule pellet from the mold.

8. The process according to claim 7 , comprising two different rods, wherein

a first rod having a plain section end for pressing the first lower half capsule pellet and

a second rod having a small hole located a center of its section end to keep the selenium and/or selenium compound at the heart of the capsule pellet during the pressing operation.

9. The process according to claim 7 , further comprising:

adding a binding agent to the at least one of selenium or selenium compound.

10. The process according to claim 9 , wherein the binding agent is a tacky organic composition, water or a combination thereof.

11. A method for preparing a selenium containing glass, comprising:

adding the selenium to the molten glass mixture as the capsule pellet according to claim 1 .

12. A method of reducing selenium burn off in a selenium comprising glass-making process, comprising: incorporating at least part of the selenium raw material for the glass by adding the capsule pellet according to claim 1 .

13. A soda lime glass comprising selenium, obtained by the method of claim 12 .

14. The soda lime glass comprising selenium according to claim 13 , wherein the glass is a float glass obtained by floating a ribbon of molten glass on an upper surface of a bath of molten metal tin.

15. A flat glass comprising selenium, wherein the flat glass is the float glass of claim 14 .