Graphite material, carbon material for battery electrode, and battery
View Patent ↗A carbon raw material such as a green coke in which loss on heat when it is heated from 300 to 1200° C. under an inert atmosphere is no less than 5% by mass and no more than 20% by mass is pulverized and then the pulverized carbon raw material is graphitized to obtain a graphite material suitable for a carbon material for anode in a lithium-ion secondary battery or the like that enables to make electrodes having a high-energy density and a large-current load characteristic since it has a small specific surface area and a small average particle diameter while maintaining high beginning efficiency and a high discharge capacity in the first round of charging and discharging. And an electrode for batteries are obtained using the graphite material.
1. A method for producing a graphite material, comprising the steps of:
pulverizing a carbon raw material which is a raw non-needle coke, which raw non-needle coke is no less than 5% mass and no more than 20% by mass in loss on heat when the carbon raw material is heated from 300 to 1200° C. under an inert atmosphere; and
then graphitizing the pulverized carbon raw material which has an average particle size of not more than 25 μm, so as to obtain a graphite material having a CTE at temperatures of 30 to 100° C. of no less than 4.0×10 −6 /° C. and no more than 5.0×10 −6 /° C.
2. The method for producing a graphite material according to claim 1 , wherein the carbon raw material is derived from petroleum or coal.
3. The method for producing a graphite material according to claim 1 , wherein the graphitization temperature is no less than 3000° C. and no more than 3300° C.
4. The method for producing a graphite material according to claim 1 , wherein the graphitization is performed in an Acheson furnace.
5. The method for producing a graphite material according to claim 1 , in which the carbon raw material is no less than 4.8×10 −6 /° C. and no more than 6.0×10 −6 /° C. in a coefficient of thermal expansion (CTE) at temperatures of 30° C. to 100° C.
6. The method for producing a graphite material according to claim 1 , further comprising the step of calcining the pulverized carbon raw material at 500° C. to 1200° C. before the graphitizing step.
7. The method for producing a graphite material according to claim 1 , in which the maximum temperature in the history of the carbon raw material before the pulverizing step is not more than 400° C.
8. The method for producing a graphite material according to claim 1 , in which the pulverized carbon raw material has an average particle size of 10 to 25 μm.