Silicone Release Compositions with Controlled Peeling Force and Silicone Release Coating Films Coated with the Same
The invention pertains to a silicone release composition of which the peeling force can be controlled and also a silicone release film coated with the composition. With the inventive composition and the release film coated with the composition, it is possible to obtain a reproducible peeling force with a given value, and also possible to produce a uniformly coated release film without discharged harmful solvent. The silicone release film produced as such can have controlled peeling force with a stable peeling force characteristic compatible with viscous agent. To this end, the invention is characterized in that the silicone release composition of which the peeling force can be controlled according to the invention is a silicone water-dispersed release coating composition, contains organopolysiloxane, organopolysiloxane resin, organo hydrogen polysiloxane and platinum chelate catalyst, and meets the following math figure for peeling force: Peeling Force=a X+b, where a=61.62±3.98, and b=16.43±3.01, X=the content(%) of organopolysiloxane resin in the release coating composition.
1 . A silicone water-dispersed release composition, comprising organopolysiloxane, organopolysiloxane resin, organo hydrogen polysiloxane and platinum chelate catalyst, wherein the organopolysiloxane comprises solid matters of 0.15 to 10 weight %, and the oranopolysiloxane resin is in water-dispersed emulsion type, and wherein the peeling force of the release coating composition can be controlled according to the following equation 1:
Peeling Force= a X+b, [Equation 1]
where a=61.62±3.98, b=16.43±3.01, and X=content (%) of organopolysiloxane resin in the silicone release composition.
2 . The composition as claimed in claim 1 , wherein the composition contains about 6 to about 20 weight % of solid matters.
3 . The composition as claimed in claim 2 , wherein the organopolysiloxane resin has a repetitive unit selected from the group consisting of:
wherein R is methyl, vinyl or phenyl, and the organopolysiloxane resin is straight-chain or circular.
4 . The composition as claimed in claim 3 , wherein the organo hydrogen polysiloxane has 0.5 to 1.2 hydrogen atoms to be coupled to a silicone atom, for one vinyl group of the organopolysiloxane, in order to achieve good compatibility with the organopolysiloxane.
5 . A silicone release film, characterized in that for the film, a silicone release coating layer is formed by coating one side or both sides of a polyester plastic film to have a given coating thickness with the silicone release composition as claimed in claim 1 , and of which the peeling force can be controlled.