Fluoropolymer coated film, process for forming the same, and fluoropolymer liquid composition
View Patent ↗A process for forming a multilayer film includes coating a polymeric substrate film with a liquid fluoropolymer coating. The liquid fluoropolymer coating includes a fluoropolymer, solvent, a compatible cross-linkable adhesive polymer, and a cross-linking agent. The process further includes cross-linking the compatible cross-linkable adhesive polymer to form a cross-linked polymer network in the fluoropolymer coating, removing the solvent from the fluoropolymer coating, and adhering the fluoropolymer coating to the polymeric substrate film. A liquid fluoropolymer coating composition includes a fluoropolymer selected from homopolymers and copolymers of vinyl fluoride and homopolymers and copolymers of vinylidene fluoride, solvent, a compatible cross-linkable adhesive polymer, and a cross-linking agent. A fluoropolymer coated film includes a polymeric substrate film and a fluoropolymer coating on the polymeric substrate film. The fluoropolymer coating includes a fluoropolymer and a compatible cross-linked adhesive polymer.
1. A fluoropolymer coated film comprising:
a polymeric substrate film; and
a fluoropolymer coating directly on the polymeric substrate film, the fluoropolymer coating comprising:
a fluoropolymer selected from the group consisting of homopolymers and copolymers of vinyl fluoride and homopolymers and copolymers of vinylidene fluoride; and
a compatible cross-linked adhesive polymer comprising functional groups selected from the group consisting of carboxylic acid, sulfonic acid, aziridine, anhydride, amine, isocyanate, melamine, epoxy, hydroxyl, and combinations thereof, wherein the compatible cross-linked adhesive polymer is selected from the group consisting of polyesters, polyester urethanes, polycarbonates, polycarbonate urethanes, acrylics, acrylic polyurethanes, polyethers, polyether urethanes, ethylene vinyl alcohol copolymers, ethylene vinyl alcohol copolymer urethanes, polyamides, polyamide urethanes, polyamide ureas, polyacrylamides, polyacrylamide urethanes and combinations thereof, wherein the fluoropolymer coating comprises interpenetrating networks of fluoropolymer and compatible cross-linked adhesive polymer and the compatible cross-linked adhesive polymer has pendant functionality capable of reacting with complementary functional groups on the substrate film surface;
wherein the polymeric substrate film comprises functional groups that interact with the compatible cross-linked adhesive polymer to promote bonding of the fluoropolymer coating to the polymeric substrate film.
2. The fluoropolymer coated film of claim 1 , wherein the fluoropolymer is selected from the group consisting of homopolymers and copolymers of vinyl fluoride comprising at least 60 mole % vinyl fluoride and homopolymers and copolymers of vinylidene fluoride comprising at least 60 mole % vinylidene fluoride.
3. The fluoropolymer coated film of claim 1 , wherein the fluoropolymer coating comprises about 1 to about 40 weight % of the compatible cross-linked adhesive polymer based on fluoropolymer solids content.
4. The fluoropolymer coated film of claim 1 , wherein the fluoropolymer coating is on both sides of the polymeric substrate film.
5. The fluoropolymer coated film of claim 1 , wherein said polymeric substrate film is unmodified polymeric substrate film.
6. The fluoropolymer coated film of claim 1 , wherein the fluoropolymer coating has a thickness of about 0.1 to about 10.0 mils.
7. The fluoropolymer coated film of claim 1 , wherein the polymeric substrate film has a thickness of about 0.5 to about 10 mils.
8. The fluoropolymer coated film of claim 1 , wherein the polymeric substrate film further comprises filler.
9. A backsheet for a photovoltaic module comprising the fluoropolymer coated film of claim 1 .
10. The fluoropolymer coated film of claim 1 , wherein the fluoropolymer coating further comprises pigment.
11. The fluoropolymer coated film of claim 10 , wherein the fluoropolymer coating comprises about 1 to about 35 weight % of pigment based on fluoropolymer solids content.
12. The fluoropolymer coated film of claim 1 , wherein the polymeric substrate film comprises polyester, polyamide, polyimide, or any combination thereof.
13. The fluoropolymer coated film of claim 12 , wherein the polymeric substrate film comprises polyester selected from the group consisting of polyethylene terephthalate, polyethylene naphthalate, and combinations thereof.